- 熔體流動速率 [g/10min]: 16.0
- 密度 [g/cm3]: 1.04
- 缺口沖擊強度: 2.6
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 2.50
- 熱變形溫度 [℃]: 105.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | mold average;Borealis Method | ||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C | 16 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 61.0 MPa | 8850 psi | H 358/30; ISO 2039 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527-2 | ||
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 5.3 % | 5.3 % | flexural strain; ISO 178 | ||
| 15 % | 15 % | ISO 527-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 2.45 GPa | 355 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 36.0 MPa | 5220 psi | 3.5% strain; ISO 178 | ||
| 38.0 MPa | 5510 psi | ISO 178 | |||
| Flexural Modulus | 2.50 GPa | 363 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 2.60 kJ/m2 @Temperature -20.0 °C | 1.24 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 6.40 kJ/m2 @Temperature 23.0 °C | 3.05 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m2 @Temperature -20.0 °C | 12.8 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1U | ||
| 93.0 kJ/m2 @Temperature 23.0 °C | 44.3 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature -20.0 °C | 19.0 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| 12.0 J/cm2 @Temperature 23.0 °C | 57.1 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.280 J/cm2 @Temperature -20.0 °C | 1.33 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.650 J/cm2 @Temperature 23.0 °C | 3.09 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 55.0 μm/m-°C | 30.6 μin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75-2 | ||
| Vicat Softening Point | 67.0 °C @Load 5.10 kg | 153 °F @Load 11.2 lb | ISO 306 | ||
| 141 °C @Load 1.02 kg | 286 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (μgC/g) | < 50 | VDA 277 | |||
| Fogging (mg) | < 2 | DIN 75201;100°C, 16h | |||
| Screw Speed | low to medium | ||||