- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 0.950
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C | 10 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 650 % | 650 % | ISO 527-3 |
| Film Elongation at Break, TD | 850 % | 850 % | ISO 527-3 |
| Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
| Secant Modulus, MD | 0.400 GPa | 58.0 ksi | ISO 527-3 |
| Secant Modulus, TD | 0.500 GPa | 72.5 ksi | ISO 527-3 |
| Impact | 59.5 | 59.5 | Damaging Force (N); ISO 7765-2 |
| Impact Test | 1.40 J | 1.03 ft-lb | Penetration Energy; ISO 7765-3 |
| Film Tensile Strength at Break, MD | 45.0 - 55.0 MPa | 6530 - 7980 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 138 - 144 °C | 280 - 291 °F | ISO 3146 |
| Vicat Softening Point | 130 °C | 266 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.5 % | <= 1.5 % | ASTM D1003 |
| Gloss | >= 130 % | >= 130 % | At 20°C; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |