- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 0.800
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 700 % | 700 % | ISO 527-3 |
| Film Elongation at Break, TD | 800 % | 800 % | ISO 527-3 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
| Secant Modulus, MD | 0.750 GPa | 109 ksi | ISO 527-3 |
| Secant Modulus, TD | 0.850 GPa | 123 ksi | ISO 527-3 |
| Impact | 34 | 34 | Damaging Force (N); ISO 7765-2 |
| Impact Test | 5.00 J | 3.69 ft-lb | Penetration Energy; ISO 7765-2 |
| Coefficient of Friction | >= 0.70 | >= 0.70 | Film/Film; ISO 8295 |
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 143 - 147 °C | 289 - 297 °F | ISO 3146 |
| Vicat Softening Point | 125 °C | 257 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 8.0 % | <= 8.0 % | ASTM D1003 |
| Gloss | >= 70 % | >= 70 % | At 20°C; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |