- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0000 MPa | 3625.94 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | At 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 0.900 GPa | 131 ksi | 1 mm/min; ISO 527 |
| Charpy Impact, Notched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179/1eA |
| 0.200 J/cm2 @Temperature -20.0 °C | 0.952 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| 0.400 J/cm2 @Temperature 0.000 °C | 1.90 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | >= 6.0 ohm | >= 6.0 ohm | DIN 53482/VDE 0303 Part 2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 1.50 μm/m-°C @Temperature 0.000 - 70.0 °C | 0.833 μin/in-°F @Temperature 32.0 - 158 °F | DIN 53752 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | DIN 52612 Part 1 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Die Temperature | 210 - 220 °C | 410 - 428 °F | |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |
| Head Temperature | 210 - 220 °C | 410 - 428 °F | |