- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 30.0
- 熱變形溫度 [℃]: 96.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 0.50 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.50 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.000 MPa | 4351.1 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | At 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | ISO 527 |
| Charpy Impact, Notched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179/1eA |
| 0.500 J/cm2 @Temperature -20.0 °C | 2.38 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | HDT; ISO 75 B |
| Vicat Softening Point | 91.0 °C | 196 °F | B (50 N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 190 - 230 °C | 374 - 446 °F | |
| Die Temperature | 200 - 230 °C | 392 - 446 °F | |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | |
| Head Temperature | 200 - 230 °C | 392 - 446 °F | |