- 熔體流動速率 [g/10min]: 12.0
- 缺口沖擊強度: 0.3
- 拉伸強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 1.20
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | 0.030 in; UL 94 |
| Flammability, UL94 | V-2 @Thickness 0.780 mm | V-2 @Thickness 0.0307 in | |
| V-2 @Thickness 1.57 mm | V-2 @Thickness 0.0618 in | ||
| V-2 @Thickness 3.05 mm | V-2 @Thickness 0.120 in | ||