- 密度 [g/cm3]: 1.28
- 缺口沖擊強度: 0.27
- 彎曲強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 6.00
- 硬度: 82.0
- 熱變形溫度 [℃]: 143.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in3 | |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 82 | 82 | ASTM D785 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 6.1 % | 6.1 % | ASTM D638 |
| Flexural Strength | 46.0 MPa | 6670 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 221 °C | 410 - 430 °F | Approximate middle barrel temperature range |