- 拉伸強度 [MPa]: 25.9
- 彎曲模量 [MPa]: 1.29
- 熱變形溫度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | ASTM D1693 |
| Melt Index of Compound | 17 g/10 min | 17 g/10 min | 2.16/230; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.9 MPa | 3760 psi | 2"/min; ASTM D638 |
| Elongation at Break | 30 % | 30 % | 2"/min; ASTM D638 |
| Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
| Impact Test | 19.0 J @Thickness 3.17 mm, Temperature 23.0 °C | 14.0 ft-lb @Thickness 0.125 in, Temperature 73.4 °F | ARM impact |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |