- 密度 [g/cm3]: 1.17
- 缺口沖擊強度: 1.23
- 彎曲強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 3.00
- 硬度: 86.0
- 熱變形溫度 [℃]: 164.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 225 °C | 437 °F | Approximate middle barrel temperature. |