- 熔體流動速率 [g/10min]: 10.0
- 缺口沖擊強度: 1.06
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.00
- 熱變形溫度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | 0.030 in; UL 94 |
| Flammability, UL94 | V-2 @Thickness 0.780 mm | V-2 @Thickness 0.0307 in | |
| V-2 @Thickness 1.57 mm | V-2 @Thickness 0.0618 in | ||
| V-2 @Thickness 3.05 mm | V-2 @Thickness 0.120 in | ||