- 熔體流動(dòng)速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.9
- 拉伸強(qiáng)度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.31
- 熱變形溫度 [℃]: 87.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1505 | ||
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | ASTM D-2240 | ||
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | >= 500 % | >= 500 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Yield | 15 % | 15 % | 2 in/min (20 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.31 GPa | 190 ksi | Secant @ 1% strain; ASTM D-790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||