- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 13.8
- 斷裂伸長率 [%]: 12.0
- 彎曲強度 [MPa]: 11.0
- 彎曲模量 [MPa]: 0.700
- 硬度: 53.0
- 熱變形溫度 [℃]: 51.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 1.09 g/cc | 0.0325 - 0.0394 lb/in3 | Average value: 0.972 g/cc Grade Count:40 |
| Filler Content | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00800 - 0.0190 cm/cm | 0.00800 - 0.0190 in/in | Average value: 0.0141 cm/cm Grade Count:35 |
| Melt Flow | 1.00 - 21.0 g/10 min | 1.00 - 21.0 g/10 min | Average value: 11.9 g/10 min Grade Count:32 |
| Ash | 9.80 - 33.0 % | 9.80 - 33.0 % | Average value: 13.0 % Grade Count:16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 53.0 - 97.0 | 53.0 - 97.0 | Average value: 79.4 Grade Count:14 |
| Hardness, Shore D | 66.0 - 74.0 | 66.0 - 74.0 | Average value: 68.7 Grade Count:3 |
| Tensile Strength, Ultimate | 11.0 - 32.1 MPa | 1600 - 4650 psi | Average value: 20.8 MPa Grade Count:19 |
| Tensile Strength, Yield | 13.8 - 52.0 MPa | 2000 - 7540 psi | Average value: 26.6 MPa Grade Count:33 |
| Elongation at Break | 2.00 - 545 % | 2.00 - 545 % | Average value: 116 % Grade Count:26 |
| Elongation at Yield | 2.80 - 100 % | 2.80 - 100 % | Average value: 14.0 % Grade Count:19 |
| Modulus of Elasticity | 0.900 - 2.14 GPa | 131 - 310 ksi | Average value: 1.38 GPa Grade Count:15 |
| Flexural Yield Strength | 12.0 - 85.0 MPa | 1740 - 12300 psi | Average value: 35.9 MPa Grade Count:21 |
| Flexural Modulus | 0.700 - 3.00 GPa | 102 - 435 ksi | Average value: 1.45 GPa Grade Count:40 |
| Izod Impact, Notched | 0.267 - 6.51 J/cm | 0.500 - 12.2 ft-lb/in | Average value: 1.12 J/cm Grade Count:35 |
| Izod Impact, Unnotched | 4.27 - 16.0 J/cm | 8.00 - 30.0 ft-lb/in | Average value: 10.5 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 3.50 - 18.0 kJ/m2 | 1.67 - 8.57 ft-lb/in2 | Average value: 8.53 kJ/m2 Grade Count:3 |
| 2.20 - 2.20 kJ/m2 @Temperature -40.0 - -40.0 °C | 1.05 - 1.05 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 2.20 kJ/m2 Grade Count:1 | |
| Charpy Impact, Notched | 0.400 - 0.400 J/cm2 @Temperature -20.0 - -20.0 °C | 1.90 - 1.90 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 0.400 J/cm2 Grade Count:1 |
| Gardner Impact | 0.780 - 190 J | 0.575 - 140 ft-lb | Average value: 29.5 J Grade Count:14 |
| 13.7842 - 13.7842 J @Temperature -30.0 - -30.0 °C | 10.1667 - 10.1667 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 13.8 J Grade Count:1 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 51.1 - 135 °C | 124 - 275 °F | Average value: 91.3 °C Grade Count:30 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 - 125 °C | 100 - 257 °F | Average value: 61.7 °C Grade Count:22 |
| Vicat Softening Point | 87.0 - 148 °C | 189 - 298 °F | Average value: 117 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 200 - 224 °C | 392 - 435 °F | Average value: 207 °C Grade Count:3 |
| Melt Temperature | 170 - 279 °C | 338 - 534 °F | Average value: 205 °C Grade Count:6 |
| Mold Temperature | 15.6 - 65.6 °C | 60.0 - 150 °F | Average value: 40.5 °C Grade Count:4 |
| Drying Temperature | 79.4 - 82.2 °C | 175 - 180 °F | Average value: 80.2 °C Grade Count:5 |
| Dry Time | 1.00 - 3.00 hour | 1.00 - 3.00 hour | Average value: 1.70 hour Grade Count:5 |