- 熔體流動(dòng)速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.02
- 缺口沖擊強(qiáng)度: 0.214
- 拉伸強(qiáng)度 [MPa]: 15.0
- 斷裂伸長率 [%]: 22.0
- 彎曲強(qiáng)度 [MPa]: 14.0
- 彎曲模量 [MPa]: 3.00
- 硬度: 33.0
- 熱變形溫度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 - 1.27 g/cc | 0.0423 - 0.0459 lb/in3 | Average value: 1.22 g/cc Grade Count:24 |
| Filler Content | 35.0 - 40.0 % | 35.0 - 40.0 % | Average value: 39.4 % Grade Count:9 |
| Water Absorption | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0325 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00400 - 0.0130 cm/cm | 0.00400 - 0.0130 in/in | Average value: 0.00690 cm/cm Grade Count:23 |
| Melt Flow | 2.00 - 17.0 g/10 min | 2.00 - 17.0 g/10 min | Average value: 9.79 g/10 min Grade Count:19 |
| Ash | 40.0 % | 40.0 % | Average value: 40.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 42.0 - 72.0 | 42.0 - 72.0 | Average value: 61.3 Grade Count:3 |
| Hardness, Rockwell R | 33.0 - 104 | 33.0 - 104 | Average value: 61.8 Grade Count:13 |
| Hardness, Shore D | 70.0 - 73.0 | 70.0 - 73.0 | Average value: 72.0 Grade Count:4 |
| Tensile Strength, Ultimate | 14.0 - 32.4 MPa | 2030 - 4700 psi | Average value: 26.6 MPa Grade Count:20 |
| 12.0 - 18.0 MPa @Temperature 60.0 - 90.0 °C | 1740 - 2610 psi @Temperature 140 - 194 °F | Average value: 15.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 15.0 - 46.9 MPa | 2180 - 6800 psi | Average value: 31.3 MPa Grade Count:14 |
| Elongation at Break | 3.00 - 10.0 % | 3.00 - 10.0 % | Average value: 6.29 % Grade Count:14 |
| Elongation at Yield | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 2.91 % Grade Count:11 |
| Modulus of Elasticity | 2.50 - 4.83 GPa | 363 - 700 ksi | Average value: 3.83 GPa Grade Count:11 |
| Flexural Yield Strength | 22.0 - 65.0 MPa | 3190 - 9430 psi | Average value: 42.9 MPa Grade Count:15 |
| Flexural Modulus | 3.00 - 7.60 GPa | 435 - 1100 ksi | Average value: 4.71 GPa Grade Count:25 |
| 0.930 - 2.80 GPa @Temperature 60.0 - 90.0 °C | 135 - 406 ksi @Temperature 140 - 194 °F | Average value: 1.87 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.214 - 1.07 J/cm | 0.400 - 2.00 ft-lb/in | Average value: 0.432 J/cm Grade Count:24 |
| 0.120 - 0.120 J/cm @Temperature -20.0 - -20.0 °C | 0.225 - 0.225 ft-lb/in @Temperature -4.00 - -4.00 °F | Average value: 0.120 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.60 - 5.34 J/cm | 3.00 - 10.0 ft-lb/in | Average value: 2.76 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 1.90 - 1.90 kJ/m2 @Temperature -40.0 - -40.0 °C | 0.904 - 0.904 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 1.90 kJ/m2 Grade Count:1 |
| Charpy Impact Unnotched | 0.400 - 0.500 J/cm2 @Temperature -40.0 - -20.0 °C | 1.90 - 2.38 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.450 J/cm2 Grade Count:1 |
| Gardner Impact | 0.300 - 2.26 J | 0.221 - 1.67 ft-lb | Average value: 1.01 J Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 - 149 °C | 214 - 300 °F | Average value: 129 °C Grade Count:22 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 - 113 °C | 145 - 235 °F | Average value: 85.4 °C Grade Count:21 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 218 - 238 °C | 425 - 460 °F | Average value: 229 °C Grade Count:5 |
| Melt Temperature | 191 - 249 °C | 375 - 480 °F | Average value: 224 °C Grade Count:7 |
| Mold Temperature | 26.7 - 70.0 °C | 80.0 - 158 °F | Average value: 44.6 °C Grade Count:8 |
| Drying Temperature | 65.6 - 100 °C | 150 - 212 °F | Average value: 78.2 °C Grade Count:7 |
| Dry Time | 1.00 - 3.00 hour | 1.00 - 3.00 hour | Average value: 1.93 hour Grade Count:7 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:4 |
| Injection Pressure | 2.76 - 103 MPa | 400 - 15000 psi | Average value: 33.1 MPa Grade Count:6 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:4 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:4 |