- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.214
- 拉伸強度 [MPa]: 15.0
- 斷裂伸長率 [%]: 21.0
- 彎曲強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 2.10
- 硬度: 30.0
- 熱變形溫度 [℃]: 97.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.49 g/cc | 0.0390 - 0.0538 lb/in3 | Average value: 1.12 g/cc Grade Count:25 |
| Filler Content | 25.0 - 40.0 % | 25.0 - 40.0 % | Average value: 27.3 % Grade Count:11 |
| Water Absorption | 0.0200 - 0.0300 % | 0.0200 - 0.0300 % | Average value: 0.0267 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00400 - 0.0130 cm/cm | 0.00400 - 0.0130 in/in | Average value: 0.00838 cm/cm Grade Count:24 |
| Melt Flow | 4.00 - 20.0 g/10 min | 4.00 - 20.0 g/10 min | Average value: 11.1 g/10 min Grade Count:16 |
| Ash | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 30.0 - 98.0 | 30.0 - 98.0 | Average value: 65.3 Grade Count:12 |
| Hardness, Shore D | 72.0 - 73.0 | 72.0 - 73.0 | Average value: 72.4 Grade Count:5 |
| Tensile Strength, Ultimate | 14.0 - 33.8 MPa | 2030 - 4900 psi | Average value: 26.0 MPa Grade Count:21 |
| Tensile Strength, Yield | 15.0 - 41.4 MPa | 2180 - 6000 psi | Average value: 29.8 MPa Grade Count:13 |
| Elongation at Break | 2.50 - 15.0 % | 2.50 - 15.0 % | Average value: 8.81 % Grade Count:18 |
| Elongation at Yield | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 3.33 % Grade Count:12 |
| Modulus of Elasticity | 2.00 - 6.21 GPa | 290 - 900 ksi | Average value: 3.49 GPa Grade Count:13 |
| Flexural Yield Strength | 21.0 - 51.7 MPa | 3050 - 7500 psi | Average value: 42.2 MPa Grade Count:17 |
| Flexural Modulus | 2.10 - 5.52 GPa | 305 - 800 ksi | Average value: 3.31 GPa Grade Count:25 |
| Izod Impact, Notched | 0.214 - 1.49 J/cm | 0.400 - 2.80 ft-lb/in | Average value: 0.523 J/cm Grade Count:25 |
| Izod Impact, Unnotched | 1.07 - 6.41 J/cm | 2.00 - 12.0 ft-lb/in | Average value: 3.51 J/cm Grade Count:8 |
| Gardner Impact | 0.451 - 2.26 J | 0.333 - 1.67 ft-lb | Average value: 1.13 J Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 - 149 °C | 207 - 300 °F | Average value: 121 °C Grade Count:20 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 130 °C | 131 - 266 °F | Average value: 80.4 °C Grade Count:23 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 216 - 232 °C | 420 - 450 °F | Average value: 222 °C Grade Count:5 |
| Melt Temperature | 191 - 243 °C | 375 - 470 °F | Average value: 218 °C Grade Count:9 |
| Mold Temperature | 26.7 - 65.6 °C | 80.0 - 150 °F | Average value: 42.7 °C Grade Count:9 |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | Average value: 76.4 °C Grade Count:9 |
| Dry Time | 1.00 - 2.00 hour | 1.00 - 2.00 hour | Average value: 1.72 hour Grade Count:9 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:5 |
| Injection Pressure | 2.76 - 103 MPa | 400 - 15000 psi | Average value: 41.9 MPa Grade Count:9 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:5 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:5 |