- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 40.5
- 斷裂伸長率 [%]: 50.0
- 彎曲強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 2.80
- 硬度: 82.0
- 熱變形溫度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 1.56 g/cc | 0.0397 - 0.0564 lb/in3 | Average value: 1.22 g/cc Grade Count:137 |
| Filler Content | 35.0 - 50.0 % | 35.0 - 50.0 % | Average value: 39.8 % Grade Count:54 |
| Water Absorption | 0.0100 - 0.0700 % | 0.0100 - 0.0700 % | Average value: 0.0417 % Grade Count:23 |
| Additive Loading | 40.0 % | 40.0 % | Average value: 40.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000300 - 0.0350 cm/cm | 0.000300 - 0.0350 in/in | Average value: 0.00322 cm/cm Grade Count:108 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00400 cm/cm | 0.00300 - 0.00400 in/in | Average value: 0.00386 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0165 cm/cm | 0.00500 - 0.0165 in/in | Average value: 0.00969 cm/cm Grade Count:8 |
| Melt Flow | 1.00 - 25.0 g/10 min | 1.00 - 25.0 g/10 min | Average value: 5.59 g/10 min Grade Count:79 |
| Ash | 28.0 - 40.0 % | 28.0 - 40.0 % | Average value: 37.3 % Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 58.0 - 72.0 | 58.0 - 72.0 | Average value: 62.5 Grade Count:4 |
| Hardness, Rockwell R | 82.0 - 116 | 82.0 - 116 | Average value: 105 Grade Count:34 |
| Hardness, Shore D | 74.0 - 85.0 | 74.0 - 85.0 | Average value: 76.6 Grade Count:17 |
| Tensile Strength, Ultimate | 30.0 - 145 MPa | 4350 - 21000 psi | Average value: 92.1 MPa Grade Count:89 |
| 63.0 - 175.816 MPa @Temperature -40.0 - 93.3 °C | 9140 - 25500.0 psi @Temperature -40.0 - 200 °F | Average value: 84.5 MPa Grade Count:8 | |
| Tensile Strength, Yield | 40.5 - 125 MPa | 5870 - 18100 psi | Average value: 88.8 MPa Grade Count:57 |
| Elongation at Break | 1.00 - 10.0 % | 1.00 - 10.0 % | Average value: 3.32 % Grade Count:95 |
| 1.80 - 2.50 % @Temperature -40.0 - 93.3 °C | 1.80 - 2.50 % @Temperature -40.0 - 200 °F | Average value: 2.25 % Grade Count:8 | |
| Elongation at Yield | 1.00 - 6.70 % | 1.00 - 6.70 % | Average value: 3.58 % Grade Count:31 |
| Modulus of Elasticity | 3.59 - 12.4 GPa | 520 - 1800 ksi | Average value: 8.15 GPa Grade Count:65 |
| 5.68817 - 11.6521 GPa @Temperature -40.0 - 93.3 °C | 825.013 - 1690.03 ksi @Temperature -40.0 - 200 °F | Average value: 6.98 GPa Grade Count:8 | |
| Flexural Yield Strength | 50.0 - 210 MPa | 7250 - 30500 psi | Average value: 137 MPa Grade Count:110 |
| 99.2845 - 293.717 MPa @Temperature -40.0 - 93.3 °C | 14400.0 - 42600.1 psi @Temperature -40.0 - 200 °F | Average value: 164 MPa Grade Count:2 | |
| Flexural Modulus | 2.80 - 12.5 GPa | 406 - 1810 ksi | Average value: 6.96 GPa Grade Count:138 |
| 4.44022 - 11.3763 GPa @Temperature -40.0 - 121 °C | 644.010 - 1650.03 ksi @Temperature -40.0 - 250 °F | Average value: 6.66 GPa Grade Count:3 | |
| Compressive Yield Strength | 61.4 - 86.2 MPa | 8900 - 12500 psi | Average value: 69.6 MPa Grade Count:3 |
| Izod Impact, Notched | 0.427 - 7.52 J/cm | 0.800 - 14.1 ft-lb/in | Average value: 1.32 J/cm Grade Count:110 |
| 0.500 - 3.84408 J/cm @Temperature -40.0 - 93.3 °C | 0.937 - 7.20154 ft-lb/in @Temperature -40.0 - 200 °F | Average value: 1.61 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 1.49 - 9.08 J/cm | 2.79 - 17.0 ft-lb/in | Average value: 5.61 J/cm Grade Count:42 |
| 3.70 - 3.70 J/cm @Temperature -40.0 - -40.0 °C | 6.93 - 6.93 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 3.70 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 11.0 - 26.0 kJ/m2 | 5.23 - 12.4 ft-lb/in2 | Average value: 20.2 kJ/m2 Grade Count:6 |
| 10.0 - 23.0 kJ/m2 @Temperature -30.0 - -20.0 °C | 4.76 - 10.9 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 16.0 kJ/m2 Grade Count:3 | |
| Charpy Impact Unnotched | 1.50 - 7.50 J/cm2 | 7.14 - 35.7 ft-lb/in2 | Average value: 5.32 J/cm2 Grade Count:23 |
| 3.80 - 8.00 J/cm2 @Temperature -30.0 - -20.0 °C | 18.1 - 38.1 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 5.22 J/cm2 Grade Count:17 | |
| Charpy Impact, Notched | 0.300 - 4.50 J/cm2 | 1.43 - 21.4 ft-lb/in2 | Average value: 1.76 J/cm2 Grade Count:30 |
| 0.400 - 3.80 J/cm2 @Temperature -30.0 - -20.0 °C | 1.90 - 18.1 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 1.62 J/cm2 Grade Count:21 | |
| Gardner Impact | 0.113 - 1.13 J | 0.0830 - 0.830 ft-lb | Average value: 0.476 J Grade Count:26 |
| Dart Drop, Total Energy | 6.34 - 15.5 J | 4.68 - 11.4 ft-lb | Average value: 12.6 J Grade Count:3 |
| 5.76 - 13.7 J @Temperature -20.0 - -20.0 °C | 4.25 - 10.1 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 9.73 J Grade Count:1 | |
| 5.76 - 13.7 J @Thickness 3.18 - 3.18 mm | 4.25 - 10.1 ft-lb @Thickness 0.125 - 0.125 in | Average value: 9.73 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 3.00e+16 ohm-cm | 1.00e+14 - 3.00e+16 ohm-cm | Average value: 8.08e+15 ohm-cm Grade Count:16 |
| Dielectric Constant | 2.75 - 3.20 | 2.75 - 3.20 | Average value: 3.03 Grade Count:5 |
| Dielectric Strength | 19.7 - 25.0 kV/mm | 500 - 635 kV/in | Average value: 21.1 kV/mm Grade Count:11 |
| Dissipation Factor | 0.00100 - 0.00200 | 0.00100 - 0.00200 | Average value: 0.00140 Grade Count:5 |
| Arc Resistance | 102 - 122 sec | 102 - 122 sec | Average value: 109 sec Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 50.0 μm/m-°C | 11.1 - 27.8 μin/in-°F | Average value: 32.5 μm/m-°C Grade Count:19 |
| Thermal Conductivity | 0.346 - 0.360 W/m-K | 2.40 - 2.50 BTU-in/hr-ft2-°F | Average value: 0.355 W/m-K Grade Count:3 |
| Melting Point | 160 - 182 °C | 320 - 360 °F | Average value: 165 °C Grade Count:27 |
| Maximum Service Temperature, Air | 65.0 - 140 °C | 149 - 284 °F | Average value: 113 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 - 166 °C | 248 - 331 °F | Average value: 159 °C Grade Count:78 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 175 °C | 149 - 347 °F | Average value: 149 °C Grade Count:116 |
| Deflection Temperature at 8.0 MPa | 125 - 138 °C | 257 - 280 °F | Average value: 134 °C Grade Count:9 |
| Vicat Softening Point | 90.0 - 189 °C | 194 - 372 °F | Average value: 149 °C Grade Count:15 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:49 |
| Flammability Test | 0.900 - 125 | 0.900 - 125 | Average value: 32.2 Grade Count:6 |
| Oxygen Index | 20.0 - 21.0 % | 20.0 - 21.0 % | Average value: 20.3 % Grade Count:3 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 741 °C Grade Count:10 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 30.0 - 280 °C | 86.0 - 536 °F | Average value: 131 °C Grade Count:25 |
| Feed Temperature | 20.0 - 240 °C | 68.0 - 464 °F | Average value: 60.9 °C Grade Count:17 |
| Nozzle Temperature | 204 - 249 °C | 400 - 480 °F | Average value: 229 °C Grade Count:16 |
| Die Temperature | 210 - 290 °C | 410 - 554 °F | Average value: 260 °C Grade Count:13 |
| Melt Temperature | 190 - 290 °C | 374 - 554 °F | Average value: 237 °C Grade Count:60 |
| Mold Temperature | 15.0 - 100 °C | 59.0 - 212 °F | Average value: 52.2 °C Grade Count:60 |
| Injection Velocity | 13.0 - 3330 mm/sec | 0.512 - 131 in/sec | Average value: 450 mm/sec Grade Count:6 |
| Drying Temperature | 65.6 - 100 °C | 150 - 212 °F | Average value: 82.1 °C Grade Count:48 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.57 hour Grade Count:42 |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.127 % Grade Count:29 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 66.1 MPa Grade Count:58 |
| Hold Pressure | 2.07 - 83.0 MPa | 300 - 12000 psi | Average value: 34.7 MPa Grade Count:25 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 2.88 MPa Grade Count:32 |
| Screw Speed | 20.0 - 150 rpm | 20.0 - 150 rpm | Average value: 41.8 rpm Grade Count:17 |
| Hot-Working Temperature | 230 - 290 °C | 446 - 554 °F | Average value: 268 °C Grade Count:10 |