- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.905
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 10.0
- 斷裂伸長率 [%]: 14.0
- 彎曲強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.270
- 硬度: 43.0
- 熱變形溫度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 - 3.15 g/cc | 0.0327 - 0.114 lb/in3 | Average value: 1.20 g/cc Grade Count:225 |
| Filler Content | 10.0 - 75.0 % | 10.0 - 75.0 % | Average value: 45.1 % Grade Count:21 |
| Water Absorption | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:3 |
| Maximum Moisture Content | 0.0100 | 0.0100 | Average value: 0.0100 Grade Count:19 |
| Linear Mold Shrinkage | 0.000900 - 0.0600 cm/cm | 0.000900 - 0.0600 in/in | Average value: 0.00946 cm/cm Grade Count:163 |
| Linear Mold Shrinkage, Transverse | 0.00460 - 0.0150 cm/cm | 0.00460 - 0.0150 in/in | Average value: 0.0118 cm/cm Grade Count:26 |
| Melt Flow | 0.500 - 100 g/10 min | 0.500 - 100 g/10 min | Average value: 14.7 g/10 min Grade Count:211 |
| Ash | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 25.0 % Grade Count:40 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 35.0 - 75.0 | 35.0 - 75.0 | Average value: 55.7 Grade Count:3 |
| Hardness, Rockwell R | 43.0 - 104 | 43.0 - 104 | Average value: 78.2 Grade Count:54 |
| Hardness, Shore D | 55.0 - 78.0 | 55.0 - 78.0 | Average value: 71.3 Grade Count:24 |
| Ball Indentation Hardness | 23.0 - 90.0 MPa | 3340 - 13100 psi | Average value: 49.5 MPa Grade Count:24 |
| Tensile Strength, Ultimate | 10.0 - 59.0 MPa | 1450 - 8560 psi | Average value: 23.3 MPa Grade Count:124 |
| 4.00 - 16.0 MPa @Temperature 60.0 - 120 °C | 580 - 2320 psi @Temperature 140 - 248 °F | Average value: 11.0 MPa Grade Count:3 | |
| Tensile Strength, Yield | 10.0 - 85.3 MPa | 1450 - 12400 psi | Average value: 27.0 MPa Grade Count:161 |
| Elongation at Break | 1.60 - 500 % | 1.60 - 500 % | Average value: 45.6 % Grade Count:162 |
| Elongation at Yield | 2.00 - 100 % | 2.00 - 100 % | Average value: 9.48 % Grade Count:97 |
| Modulus of Elasticity | 0.950 - 5.40 GPa | 138 - 783 ksi | Average value: 2.37 GPa Grade Count:133 |
| Flexural Yield Strength | 14.0 - 127 MPa | 2030 - 18500 psi | Average value: 38.7 MPa Grade Count:140 |
| Flexural Modulus | 0.270 - 9.00 GPa | 39.1 - 1310 ksi | Average value: 2.46 GPa Grade Count:196 |
| 0.280 - 1.25 GPa @Temperature 60.0 - 120 °C | 40.6 - 181 ksi @Temperature 140 - 248 °F | Average value: 0.717 GPa Grade Count:3 | |
| Izod Impact, Notched | 0.200 - 100 J/cm | 0.375 - 187 ft-lb/in | Average value: 0.637 J/cm Grade Count:119 |
| 0.150 - 10.0 J/cm @Temperature -40.0 - 0.000 °C | 0.281 - 18.7 ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 0.474 J/cm Grade Count:15 | |
| 0.196133 - 0.220 J/cm @Temperature -30.0 - -10.0 °C | 0.367438 - 0.412 ft-lb/in @Temperature -22.0 - 14.0 °F | Average value: 0.474 J/cm Grade Count:10 | |
| 0.196133 - 0.220 J/cm @Thickness 3.20 - 6.40 mm | 0.367438 - 0.412 ft-lb/in @Thickness 0.126 - 0.252 in | Average value: 0.474 J/cm Grade Count:10 | |
| Izod Impact, Unnotched | 1.33 J/cm - NB | 2.49 ft-lb/in - NB | Average value: 5.56 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 2.00 - 57.0 kJ/m2 | 0.952 - 27.1 ft-lb/in2 | Average value: 16.8 kJ/m2 Grade Count:57 |
| 1.70 - 43.0 kJ/m2 @Temperature -40.0 - 10.0 °C | 0.809 - 20.5 ft-lb/in2 @Temperature -40.0 - 50.0 °F | Average value: 5.91 kJ/m2 Grade Count:28 | |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m2 - NB | 24.3 ft-lb/in2 - NB | Average value: 66.6 kJ/m2 Grade Count:7 |
| 21.0 - 200 kJ/m2 @Temperature -20.0 - -20.0 °C | 9.99 - 95.2 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 72.5 kJ/m2 Grade Count:4 | |
| Charpy Impact Unnotched | 0.700 - 1000 J/cm2 | 3.33 - 4760 ft-lb/in2 | Average value: 4.67 J/cm2 Grade Count:72 |
| 0.500 - 999.9 J/cm2 @Temperature -40.0 - -20.0 °C | 2.38 - 4759 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 3.92 J/cm2 Grade Count:47 | |
| Charpy Impact, Notched | 0.150 - 7.00 J/cm2 | 0.714 - 33.3 ft-lb/in2 | Average value: 1.51 J/cm2 Grade Count:81 |
| 0.100 - 2.00 J/cm2 @Temperature -30.0 - -20.0 °C | 0.476 - 9.52 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.427 J/cm2 Grade Count:47 | |
| Gardner Impact | 0.678 - 10.2 J | 0.500 - 7.52 ft-lb | Average value: 5.93 J Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+15 ohm-cm | 1.00e+13 - 1.00e+15 ohm-cm | Average value: 7.50e+14 ohm-cm Grade Count:22 |
| Surface Resistance | 3000 - 1.00e+15 ohm | 3000 - 1.00e+15 ohm | Average value: 1.35e+14 ohm Grade Count:23 |
| Dielectric Strength | 24.0 - 43.0 kV/mm | 610 - 1090 kV/in | Average value: 38.5 kV/mm Grade Count:13 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 596 V Grade Count:25 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 100 μm/m-°C | 16.7 - 55.6 μin/in-°F | Average value: 59.4 μm/m-°C Grade Count:17 |
| Melting Point | 160 - 168 °C | 320 - 334 °F | Average value: 165 °C Grade Count:42 |
| Maximum Service Temperature, Air | 110 - 140 °C | 230 - 284 °F | Average value: 117 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 - 156 °C | 167 - 313 °F | Average value: 116 °C Grade Count:150 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 - 145 °C | 117 - 293 °F | Average value: 69.2 °C Grade Count:171 |
| Vicat Softening Point | 36.0 - 161 °C | 96.8 - 322 °F | Average value: 113 °C Grade Count:98 |
| UL RTI, Electrical | 65.0 - 120 °C | 149 - 248 °F | Average value: 76.0 °C Grade Count:9 |
| UL RTI, Mechanical with Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 76.0 °C Grade Count:9 |
| UL RTI, Mechanical without Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 76.0 °C Grade Count:9 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:69 |
| Flammability Test | 22.0 - 22.1 | 22.0 - 22.1 | Average value: 22.1 Grade Count:4 |
| Oxygen Index | 22.0 - 27.0 % | 22.0 - 27.0 % | Average value: 25.1 % Grade Count:12 |
| Glow Wire Test | 725 - 960 °C | 1340 - 1760 °F | Average value: 862 °C Grade Count:24 |
| Shrinkage | 0.800 - 1.20 % | 0.800 - 1.20 % | Average value: 1.00 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 260 °C | 340 - 500 °F | Average value: 235 °C Grade Count:39 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 60.0 °C Grade Count:34 |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | Average value: 221 °C Grade Count:29 |
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | Average value: 216 °C Grade Count:61 |
| Mold Temperature | 20.0 - 90.0 °C | 68.0 - 194 °F | Average value: 47.8 °C Grade Count:95 |
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | Average value: 150 mm/sec Grade Count:32 |
| Drying Temperature | 70.0 - 100 °C | 158 - 212 °F | Average value: 77.8 °C Grade Count:56 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.17 hour Grade Count:47 |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.140 % Grade Count:5 |
| Injection Pressure | 29.4 - 120 MPa | 4260 - 17400 psi | Average value: 84.3 MPa Grade Count:30 |
| Hold Pressure | 3.00 - 80.0 MPa | 435 - 11600 psi | Average value: 38.7 MPa Grade Count:34 |
| Back Pressure | 0.490 - 58.8 MPa | 71.1 - 8530 psi | Average value: 24.8 MPa Grade Count:35 |
| Screw Speed | 30.0 - 60.0 rpm | 30.0 - 60.0 rpm | Average value: 46.3 rpm Grade Count:26 |