- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.85
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.107
- 拉伸強度 [MPa]: 2.07
- 斷裂伸長率 [%]: 17.9
- 彎曲強度 [MPa]: 10.3
- 彎曲模量 [MPa]: 0.621
- 硬度: 69.0
- 熱變形溫度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.850 - 1.90 g/cc | 0.0307 - 0.0686 lb/in3 | Average value: 1.10 g/cc Grade Count:240 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 23.4 % Grade Count:21 |
| Water Absorption | 0.0100 - 0.0600 % | 0.0100 - 0.0600 % | Average value: 0.0246 % Grade Count:57 |
| Maximum Moisture Content | 0.0100 - 0.0200 | 0.0100 - 0.0200 | Average value: 0.0125 Grade Count:4 |
| Linear Mold Shrinkage | 0.000100 - 0.0500 cm/cm | 0.000100 - 0.0500 in/in | Average value: 0.0142 cm/cm Grade Count:172 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00700 - 0.0200 cm/cm | 0.00700 - 0.0200 in/in | Average value: 0.0158 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00900 - 0.0243 cm/cm | 0.00900 - 0.0243 in/in | Average value: 0.0178 cm/cm Grade Count:21 |
| Melt Flow | 0.300 - 140 g/10 min | 0.300 - 140 g/10 min | Average value: 12.2 g/10 min Grade Count:171 |
| Ash | 15.0 - 25.0 % | 15.0 - 25.0 % | Average value: 20.0 % Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 100 | 100 | Average value: 100 Grade Count:4 |
| Hardness, Rockwell R | 69.0 - 105 | 69.0 - 105 | Average value: 89.7 Grade Count:20 |
| Hardness, Shore A | 66.0 - 69.0 | 66.0 - 69.0 | Average value: 67.8 Grade Count:6 |
| Hardness, Shore D | 60.0 - 80.0 | 60.0 - 80.0 | Average value: 71.0 Grade Count:30 |
| Tensile Strength, Ultimate | 10.3 - 300 MPa | 1500 - 43500 psi | Average value: 33.0 MPa Grade Count:153 |
| Tensile Strength, Yield | 2.07 - 76.0 MPa | 300 - 11000 psi | Average value: 28.8 MPa Grade Count:100 |
| Elongation at Break | 1.00 - 558 % | 1.00 - 558 % | Average value: 60.9 % Grade Count:174 |
| Elongation at Yield | 2.00 - 350 % | 2.00 - 350 % | Average value: 40.8 % Grade Count:34 |
| Modulus of Elasticity | 0.800 - 9.31 GPa | 116 - 1350 ksi | Average value: 2.09 GPa Grade Count:104 |
| Flexural Yield Strength | 17.9 - 300 MPa | 2600 - 43500 psi | Average value: 41.7 MPa Grade Count:116 |
| Flexural Modulus | 0.621 - 7.50 GPa | 90.0 - 1090 ksi | Average value: 1.87 GPa Grade Count:197 |
| Izod Impact, Notched | 0.107 J/cm - NB | 0.200 ft-lb/in - NB | Average value: 0.896 J/cm Grade Count:156 |
| 0.150 - 0.550 J/cm @Temperature -20.0 - 0.000 °C | 0.281 - 1.03 ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 0.329 J/cm Grade Count:17 | |
| Izod Impact, Unnotched | 0.300 - 5340 J/cm | 0.562 - 10000 ft-lb/in | Average value: 5.71 J/cm Grade Count:56 |
| 0.150 - 0.400 J/cm @Temperature 0.000 - 0.000 °C | 0.281 - 0.749 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.254 J/cm Grade Count:8 | |
| Izod Impact, Notched (ISO) | 2.00 - 60.0 kJ/m2 | 0.952 - 28.6 ft-lb/in2 | Average value: 7.99 kJ/m2 Grade Count:36 |
| 2.00 - 10.0 kJ/m2 @Temperature -30.0 - -20.0 °C | 0.952 - 4.76 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 4.11 kJ/m2 Grade Count:9 | |
| Izod Impact, Unnotched (ISO) | 13.0 - 13.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 6.19 - 6.19 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 13.0 kJ/m2 Grade Count:1 |
| Charpy Impact Unnotched | 1.00 J/cm2 - NB | 4.76 ft-lb/in2 - NB | Average value: 4.25 J/cm2 Grade Count:40 |
| 1.00 - 999.9 J/cm2 @Temperature -40.0 - -20.0 °C | 4.76 - 4759 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 3.34 J/cm2 Grade Count:19 | |
| Charpy Impact, Notched | 0.200 - 9.00 J/cm2 | 0.952 - 42.8 ft-lb/in2 | Average value: 0.688 J/cm2 Grade Count:46 |
| 0.100 - 1.40 J/cm2 @Temperature -30.0 - -20.0 °C | 0.476 - 6.66 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.292 J/cm2 Grade Count:24 | |
| Gardner Impact | 0.904 - 260 J | 0.667 - 192 ft-lb | Average value: 27.2 J Grade Count:22 |
| Dart Drop, Total Energy | 2.71 - 14.9 J | 2.00 - 11.0 ft-lb | Average value: 8.59 J Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+17 ohm-cm | 10.0 - 1.00e+17 ohm-cm | Average value: 4.57e+15 ohm-cm Grade Count:78 |
| Surface Resistance | 1000 - 1.00e+16 ohm | 1000 - 1.00e+16 ohm | Average value: 2.31e+15 ohm Grade Count:44 |
| Static Decay | 0.500 - 2.00 sec | 0.500 - 2.00 sec | Average value: 1.50 sec Grade Count:3 |
| Dielectric Constant | 2.10 - 3.06 | 2.10 - 3.06 | Average value: 2.55 Grade Count:8 |
| Dielectric Strength | 17.7 - 43.0 kV/mm | 450 - 1090 kV/in | Average value: 28.6 kV/mm Grade Count:49 |
| Dissipation Factor | 0.00120 - 0.0100 | 0.00120 - 0.0100 | Average value: 0.00380 Grade Count:4 |
| Arc Resistance | 60.0 - 180 sec | 60.0 - 180 sec | Average value: 124 sec Grade Count:6 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 550 V Grade Count:58 |
| Hot Wire Ignition, HWI | 7.00 - 60.0 sec | 7.00 - 60.0 sec | Average value: 26.8 sec Grade Count:4 |
| High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | Average value: 120 arcs Grade Count:4 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 330 mm/min | 0.000 - 13.0 in/min | Average value: 116 mm/min Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.8 - 64.8 μm/m-°C | 21.0 - 36.0 μin/in-°F | Average value: 55.5 μm/m-°C Grade Count:6 |
| Thermal Conductivity | 0.170 - 0.303 W/m-K | 1.18 - 2.10 BTU-in/hr-ft2-°F | Average value: 0.258 W/m-K Grade Count:3 |
| Melting Point | 130 - 170 °C | 266 - 338 °F | Average value: 162 °C Grade Count:52 |
| Maximum Service Temperature, Air | 65.0 - 130 °C | 149 - 266 °F | Average value: 93.6 °C Grade Count:6 |
| Hot Ball Pressure Test | 75.0 - 125 °C | 167 - 257 °F | Average value: 118 °C Grade Count:15 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 205 °C | 158 - 401 °F | Average value: 109 °C Grade Count:107 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.6 - 190 °C | 105 - 374 °F | Average value: 69.9 °C Grade Count:147 |
| Vicat Softening Point | 70.0 - 205 °C | 158 - 401 °F | Average value: 130 °C Grade Count:87 |
| Heat Distortion Temperature | 120 - 155 °C | 248 - 311 °F | Average value: 136 °C Grade Count:6 |
| UL RTI, Electrical | 65.0 - 125 °C | 149 - 257 °F | Average value: 114 °C Grade Count:10 |
| UL RTI, Mechanical with Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 115 °C Grade Count:7 |
| UL RTI, Mechanical without Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 113 °C Grade Count:10 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Average value: 5.50 Grade Count:221 |
| Flammability Test | 3.00 - 125 | 3.00 - 125 | Average value: 55.9 Grade Count:14 |
| Oxygen Index | 17.0 - 34.0 % | 17.0 - 34.0 % | Average value: 26.1 % Grade Count:67 |
| Glow Wire Test | 725 - 960 °C | 1340 - 1760 °F | Average value: 928 °C Grade Count:89 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 240 °C | 380 - 464 °F | Average value: 215 °C Grade Count:14 |
| Feed Temperature | 60.0 - 70.0 °C | 140 - 158 °F | Average value: 64.6 °C Grade Count:13 |
| Nozzle Temperature | 200 - 240 °C | 392 - 464 °F | Average value: 208 °C Grade Count:17 |
| Die Temperature | 32.2 - 240 °C | 90.0 - 464 °F | Average value: 133 °C Grade Count:4 |
| Melt Temperature | 160 - 302 °C | 320 - 576 °F | Average value: 206 °C Grade Count:97 |
| Mold Temperature | 4.00 - 91.0 °C | 39.2 - 196 °F | Average value: 44.6 °C Grade Count:100 |
| Drying Temperature | 51.7 - 90.0 °C | 125 - 194 °F | Average value: 74.2 °C Grade Count:78 |
| Dry Time | 1.00 - 5.00 hour | 1.00 - 5.00 hour | Average value: 2.24 hour Grade Count:66 |
| Moisture Content | 0.0100 - 0.200 % | 0.0100 - 0.200 % | Average value: 0.0794 % Grade Count:17 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 75.5 MPa Grade Count:60 |
| Hold Pressure | 2.07 - 80.0 MPa | 300 - 11600 psi | Average value: 36.9 MPa Grade Count:12 |
| Back Pressure | 0.345 - 58.8 MPa | 50.0 - 8530 psi | Average value: 9.44 MPa Grade Count:15 |
| Screw Speed | 30.0 - 60.0 rpm | 30.0 - 60.0 rpm | Average value: 46.3 rpm Grade Count:4 |