- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.123
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.26
- 拉伸強度 [MPa]: 8.96
- 斷裂伸長率 [%]: 13.4
- 彎曲強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.172
- 硬度: 33.0
- 熱變形溫度 [℃]: 35.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.123 - 2.40 g/cc | 0.00444 - 0.0867 lb/in3 | Average value: 0.950 g/cc Grade Count:686 |
| Filler Content | 0.000 - 75.0 % | 0.000 - 75.0 % | Average value: 21.1 % Grade Count:59 |
| Water Absorption | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.0777 % Grade Count:43 |
| Oxidative Induction Time (OIT) | 30.0 - 40.0 min @Temperature 190 - 220 °C | 30.0 - 40.0 min @Temperature 374 - 428 °F | Average value: 48.0 min Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.0350 cm/cm | 0.00100 - 0.0350 in/in | Average value: 0.0125 cm/cm Grade Count:196 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0250 cm/cm | 0.00500 - 0.0250 in/in | Average value: 0.0148 cm/cm Grade Count:32 |
| Melt Flow | 0.200 - 150 g/10 min | 0.200 - 150 g/10 min | Average value: 18.2 g/10 min Grade Count:858 |
| Base Resin Melt Index | 1.20 - 45.0 g/10 min @Temperature 230 - 230 °C | 1.20 - 45.0 g/10 min @Temperature 446 - 446 °F | Average value: 16.8 g/10 min Grade Count:17 |
| Antiblock Level | 1500 - 1800 ppm | 1500 - 1800 ppm | Average value: 1740 ppm Grade Count:5 |
| Slip Level | 1000 - 2100 ppm | 1000 - 2100 ppm | Average value: 1860 ppm Grade Count:9 |
| Ash | 1.00 - 40.0 % | 1.00 - 40.0 % | Average value: 15.5 % Grade Count:15 |
| 0.300 - 0.500 % @Temperature 600 - 900 °C | 0.300 - 0.500 % @Temperature 1110 - 1650 °F | Average value: 0.433 % Grade Count:3 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45.0 - 55.0 | 45.0 - 55.0 | Average value: 52.5 Grade Count:4 |
| Hardness, Rockwell R | 33.0 - 115 | 33.0 - 115 | Average value: 85.4 Grade Count:310 |
| Hardness, Shore D | 52.0 - 85.0 | 52.0 - 85.0 | Average value: 66.7 Grade Count:124 |
| Ball Indentation Hardness | 35.0 - 82.0 MPa | 5080 - 11900 psi | Average value: 62.5 MPa Grade Count:21 |
| Tensile Strength, Ultimate | 10.0 - 128 MPa | 1450 - 18500 psi | Average value: 28.0 MPa Grade Count:229 |
| 9.00 - 15.0 MPa @Temperature 60.0 - 90.0 °C | 1310 - 2180 psi @Temperature 140 - 194 °F | Average value: 12.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 8.96 - 110 MPa | 1300 - 16000 psi | Average value: 26.5 MPa Grade Count:664 |
| Film Elongation at Break, MD | 80.0 - 800 % | 80.0 - 800 % | Average value: 577 % Grade Count:19 |
| Film Elongation at Break, TD | 500 - 800 % | 500 - 800 % | Average value: 627 % Grade Count:11 |
| Elongation at Break | 1.30 - 1000 % | 1.30 - 1000 % | Average value: 191 % Grade Count:217 |
| Elongation at Yield | 0.500 - 500 % | 0.500 - 500 % | Average value: 16.7 % Grade Count:485 |
| Modulus of Elasticity | 0.300 - 13.0 GPa | 43.5 - 1890 ksi | Average value: 1.51 GPa Grade Count:203 |
| Flexural Yield Strength | 13.4 - 181 MPa | 1950 - 26300 psi | Average value: 47.6 MPa Grade Count:121 |
| Flexural Modulus | 0.172 - 11.0 GPa | 25.0 - 1600 ksi | Average value: 1.40 GPa Grade Count:768 |
| 0.370 - 0.560 GPa @Temperature 60.0 - 90.0 °C | 53.7 - 81.2 ksi @Temperature 140 - 194 °F | Average value: 0.465 GPa Grade Count:1 | |
| Shear Modulus | 0.260 - 0.730 GPa | 37.7 - 106 ksi | Average value: 0.541 GPa Grade Count:20 |
| Secant Modulus | 0.345 - 1.50 GPa | 50.0 - 218 ksi | Average value: 0.982 GPa Grade Count:3 |
| Izod Impact, Notched | 0.260 J/cm - NB | 0.487 ft-lb/in - NB | Average value: 1.37 J/cm Grade Count:592 |
| 0.160 - 99.99 J/cm @Temperature -40.0 - 4.00 °C | 0.300 - 187.3 ft-lb/in @Temperature -40.0 - 39.2 °F | Average value: 0.805 J/cm Grade Count:77 | |
| 0.200 J/cm - NB @Temperature -30.0 - 0.000 °C | 0.375 ft-lb/in - NB @Temperature -22.0 - 32.0 °F | Average value: 0.805 J/cm Grade Count:26 | |
| 0.200 J/cm - NB @Thickness 3.17 - 3.17 mm | 0.375 ft-lb/in - NB @Thickness 0.125 - 0.125 in | Average value: 0.805 J/cm Grade Count:26 | |
| 0.32034 - 1.33475 J/cm @Diameter 0.125 - 3.17 mm | 0.60013 - 2.50053 ft-lb/in @Diameter 0.00492 - 0.125 in | Average value: 0.805 J/cm Grade Count:9 | |
| 0.32034 - 1.33475 J/cm @Temperature -20.0 - 4.00 °C | 0.60013 - 2.50053 ft-lb/in @Temperature -4.00 - 39.2 °F | Average value: 0.805 J/cm Grade Count:9 | |
| Izod Impact, Unnotched | 0.294 J/cm - NB | 0.551 ft-lb/in - NB | Average value: 4.51 J/cm Grade Count:47 |
| 0.343233 - 0.441299 J/cm @Temperature -10.0 - -10.0 °C | 0.643016 - 0.826734 ft-lb/in @Temperature 14.0 - 14.0 °F | Average value: 0.392 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 4.00 - 21000 kJ/m2 | 1.90 - 9990 ft-lb/in2 | Average value: 16.4 kJ/m2 Grade Count:54 |
| 2.00 - 13.0 kJ/m2 @Temperature -40.0 - 0.000 °C | 0.952 - 6.19 ft-lb/in2 @Temperature -40.0 - 32.0 °F | Average value: 5.25 kJ/m2 Grade Count:17 | |
| Charpy Impact Unnotched | 0.800 J/cm2 - NB | 3.81 ft-lb/in2 - NB | Average value: 4.09 J/cm2 Grade Count:80 |
| 1.20 J/cm2 - NB @Temperature -40.0 - 0.000 °C | 5.71 ft-lb/in2 - NB @Temperature -40.0 - 32.0 °F | Average value: 8.38 J/cm2 Grade Count:41 | |
| Charpy Impact, Notched | 0.300 - 55.0 J/cm2 | 1.43 - 262 ft-lb/in2 | Average value: 1.80 J/cm2 Grade Count:179 |
| 0.100 - 12.0 J/cm2 @Temperature -40.0 - 0.000 °C | 0.476 - 57.1 ft-lb/in2 @Temperature -40.0 - 32.0 °F | Average value: 0.596 J/cm2 Grade Count:137 | |
| Gardner Impact | 1.25 - 136 J | 0.920 - 100 ft-lb | Average value: 22.9 J Grade Count:69 |
| 1.00 - 36.0 J @Temperature -30.0 - -20.0 °C | 0.738 - 26.6 ft-lb @Temperature -22.0 - -4.00 °F | Average value: 19.8 J Grade Count:41 | |
| 4.86 - 23.6 J @Temperature -23.0 - -20.0 °C | 3.58 - 17.4 ft-lb @Temperature -9.40 - -4.00 °F | Average value: 19.8 J Grade Count:6 | |
| 4.86 - 23.6 J @Thickness 3.17 - 3.18 mm | 3.58 - 17.4 ft-lb @Thickness 0.125 - 0.125 in | Average value: 19.8 J Grade Count:6 | |
| Dart Drop, Total Energy | 5.20 - 50.0 J | 3.84 - 36.9 ft-lb | Average value: 23.9 J Grade Count:37 |
| Falling Dart Impact | 2.26 - 33.0 J | 1.67 - 24.3 ft-lb | Average value: 9.75 J Grade Count:11 |
| 28.2011 - 28.2011 J @Temperature -30.0 - -30.0 °C | 20.8000 - 20.8000 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 13.1 J Grade Count:1 | |
| 3.00 - 27.0 J @Temperature -30.0 - -30.0 °C | 2.21 - 19.9 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 13.1 J Grade Count:5 | |
| 3.00 - 27.0 J @Thickness 3.17 - 3.17 mm | 2.21 - 19.9 ft-lb @Thickness 0.125 - 0.125 in | Average value: 13.1 J Grade Count:5 | |
| Puncture Energy | 10.0 - 48.0 J @Temperature -40.0 - 0.000 °C | 7.38 - 35.4 ft-lb @Temperature -40.0 - 32.0 °F | Average value: 23.6 J Grade Count:14 |
| Coefficient of Friction | 0.100 - 0.700 | 0.100 - 0.700 | Average value: 0.311 Grade Count:16 |
| Dart drop Total Energy | 6.73 - 7.79 J/cm | 0.0126 - 0.0146 ft-lb/mil | Average value: 7.08 J/cm Grade Count:3 |
| Film Tensile Strength at Break, MD | 21.0 - 440 MPa | 3050 - 63800 psi | Average value: 73.0 MPa Grade Count:27 |
| Film Tensile Strength at Break, TD | 25.0 - 340 MPa | 3630 - 49300 psi | Average value: 59.4 MPa Grade Count:25 |
| Tangent Modulus | 740 - 1590 MPa | 107000 - 230000 psi | Average value: 1150 MPa Grade Count:16 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 50.0 - 1.00e+17 ohm-cm | 50.0 - 1.00e+17 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:38 |
| Surface Resistance | 100 - 1.00e+16 ohm | 100 - 1.00e+16 ohm | Average value: 8.28e+14 ohm Grade Count:40 |
| Insulation Resistance | 100 - 1.00e+14 ohm | 100 - 1.00e+14 ohm | Average value: 1.11e+13 ohm Grade Count:9 |
| Dielectric Strength | 11.8 - 27.0 kV/mm | 300 - 686 kV/in | Average value: 21.5 kV/mm Grade Count:11 |
| Comparative Tracking Index | 450 - 600 V | 450 - 600 V | Average value: 585 V Grade Count:31 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.7 - 150 μm/m-°C | 6.50 - 83.3 μin/in-°F | Average value: 85.3 μm/m-°C Grade Count:29 |
| Thermal Conductivity | 0.240 - 3.40 W/m-K | 1.67 - 23.6 BTU-in/hr-ft2-°F | Average value: 0.623 W/m-K Grade Count:11 |
| Melting Point | 128 - 170 °C | 262 - 338 °F | Average value: 154 °C Grade Count:141 |
| Crystallization Temperature | 35.0 - 130 °C | 95.0 - 266 °F | Average value: 101 °C Grade Count:14 |
| Maximum Service Temperature, Air | 65.0 - 130 °C | 149 - 266 °F | Average value: 94.5 °C Grade Count:18 |
| Deflection Temperature at 0.46 MPa (66 psi) | 35.0 - 185 °C | 95.0 - 365 °F | Average value: 95.0 °C Grade Count:569 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 - 165 °C | 106 - 329 °F | Average value: 64.6 °C Grade Count:241 |
| Vicat Softening Point | 50.0 - 189 °C | 122 - 372 °F | Average value: 120 °C Grade Count:192 |
| Heat Distortion Temperature | 75.0 - 83.0 °C | 167 - 181 °F | Average value: 79.3 °C Grade Count:6 |
| UL RTI, Electrical | 105 - 115 °C | 221 - 239 °F | Average value: 108 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:112 |
| Flash Point | 340 °C | 644 °F | Average value: 340 °C Grade Count:10 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 806 °C Grade Count:50 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.500 - 40.0 % | 0.500 - 40.0 % | Average value: 9.04 % Grade Count:64 |
| Gloss | 3.00 - 150 % | 3.00 - 150 % | Average value: 102 % Grade Count:33 |
| Transmission, Visible | 80.0 - 90.0 % | 80.0 - 90.0 % | Average value: 88.9 % Grade Count:27 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 87.8 - 280 °C | 190 - 536 °F | Average value: 213 °C Grade Count:39 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 60.0 °C Grade Count:3 |
| Nozzle Temperature | 204 - 250 °C | 400 - 482 °F | Average value: 214 °C Grade Count:56 |
| Die Temperature | 175 - 230 °C | 347 - 446 °F | Average value: 210 °C Grade Count:23 |
| Melt Temperature | 16.0 - 302 °C | 60.8 - 575 °F | Average value: 216 °C Grade Count:196 |
| Head Temperature | 200 - 230 °C | 392 - 446 °F | Average value: 215 °C Grade Count:17 |
| Mold Temperature | 4.44 - 90.6 °C | 40.0 - 195 °F | Average value: 43.2 °C Grade Count:169 |
| Drying Temperature | 65.6 - 95.0 °C | 150 - 203 °F | Average value: 75.7 °C Grade Count:85 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.61 hour Grade Count:75 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.0547 % Grade Count:32 |
| Injection Pressure | 0.500 - 120 MPa | 72.5 - 17400 psi | Average value: 48.4 MPa Grade Count:87 |
| Hold Pressure | 2.07 - 80.0 MPa | 300 - 11600 psi | Average value: 20.6 MPa Grade Count:61 |
| Back Pressure | 0.000 - 2.00 MPa | 0.000 - 290 psi | Average value: 1.02 MPa Grade Count:87 |
| Clamp Pressure | 27.6 - 34.5 MPa | 4000 - 5000 psi | Average value: 31.0 MPa Grade Count:14 |
| Component Elements Properties | Metric | English | Comments |
| SiO2 | 0.180 % | 0.180 % | Average value: 0.180 % Grade Count:5 |