- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.93
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 21.0
- 斷裂伸長率 [%]: 29.0
- 彎曲強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 1.20
- 硬度: 76.0
- 熱變形溫度 [℃]: 65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 - 1.45 g/cc | 0.0336 - 0.0524 lb/in3 | Average value: 1.01 g/cc Grade Count:110 |
| Filler Content | 5.00 - 15.0 % | 5.00 - 15.0 % | Average value: 10.4 % Grade Count:60 |
| Water Absorption | 0.0100 - 0.150 % | 0.0100 - 0.150 % | Average value: 0.0190 % Grade Count:20 |
| Additive Loading | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.0390 cm/cm | 0.00200 - 0.0390 in/in | Average value: 0.00757 cm/cm Grade Count:96 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00900 - 0.0120 cm/cm | 0.00900 - 0.0120 in/in | Average value: 0.00956 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00620 - 0.0210 cm/cm | 0.00620 - 0.0210 in/in | Average value: 0.0156 cm/cm Grade Count:8 |
| Melt Flow | 1.00 - 20.0 g/10 min | 1.00 - 20.0 g/10 min | Average value: 8.73 g/10 min Grade Count:74 |
| Ash | 10.0 - 29.0 % | 10.0 - 29.0 % | Average value: 12.8 % Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 76.0 - 110 | 76.0 - 110 | Average value: 90.4 Grade Count:28 |
| Hardness, Shore D | 32.0 - 73.0 | 32.0 - 73.0 | Average value: 69.3 Grade Count:23 |
| Tensile Strength, Ultimate | 20.0 - 115 MPa | 2900 - 16700 psi | Average value: 43.7 MPa Grade Count:77 |
| Tensile Strength, Yield | 21.0 - 60.0 MPa | 3050 - 8700 psi | Average value: 42.1 MPa Grade Count:35 |
| Elongation at Break | 2.00 - 34.0 % | 2.00 - 34.0 % | Average value: 7.35 % Grade Count:68 |
| Elongation at Yield | 2.00 - 10.0 % | 2.00 - 10.0 % | Average value: 4.78 % Grade Count:20 |
| Modulus of Elasticity | 1.70 - 5.17 GPa | 247 - 750 ksi | Average value: 2.97 GPa Grade Count:46 |
| Flexural Yield Strength | 29.0 - 165 MPa | 4200 - 23900 psi | Average value: 59.2 MPa Grade Count:74 |
| Flexural Modulus | 1.20 - 6.00 GPa | 174 - 870 ksi | Average value: 2.44 GPa Grade Count:105 |
| Compressive Yield Strength | 47.6 - 52.4 MPa | 6900 - 7600 psi | Average value: 49.1 MPa Grade Count:4 |
| Izod Impact, Notched | 0.267 - 3.74 J/cm | 0.500 - 7.00 ft-lb/in | Average value: 0.733 J/cm Grade Count:92 |
| Izod Impact, Unnotched | 1.33 - 5340 J/cm | 2.50 - 10000 ft-lb/in | Average value: 4.39 J/cm Grade Count:41 |
| Izod Impact, Notched (ISO) | 10.0 - 10.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 4.76 - 4.76 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 10.0 kJ/m2 Grade Count:1 |
| Charpy Impact Unnotched | 2.00 - 5.00 J/cm2 | 9.52 - 23.8 ft-lb/in2 | Average value: 3.80 J/cm2 Grade Count:8 |
| 2.00 - 3.00 J/cm2 @Temperature -20.0 - -20.0 °C | 9.52 - 14.3 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 2.45 J/cm2 Grade Count:8 | |
| Charpy Impact, Notched | 0.250 - 1.50 J/cm2 | 1.19 - 7.14 ft-lb/in2 | Average value: 0.813 J/cm2 Grade Count:15 |
| 0.100 - 0.700 J/cm2 @Temperature -20.0 - -20.0 °C | 0.476 - 3.33 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 0.319 J/cm2 Grade Count:12 | |
| Gardner Impact | 0.339 - 4.51 J | 0.250 - 3.33 ft-lb | Average value: 1.02 J Grade Count:29 |
| 1.90 - 1.90 J @Temperature -20.0 - -20.0 °C | 1.40 - 1.40 ft-lb @Temperature -4.00 - -4.00 °F | Average value: 1.90 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+17 ohm-cm | 1000 - 1.00e+17 ohm-cm | Average value: 8.62e+15 ohm-cm Grade Count:26 |
| Surface Resistance | 100000 - 1.00e+15 ohm | 100000 - 1.00e+15 ohm | Average value: 1.67e+14 ohm Grade Count:9 |
| Static Decay | 1.00 - 2.00 sec | 1.00 - 2.00 sec | Average value: 1.86 sec Grade Count:7 |
| Dielectric Constant | 2.50 - 2.90 | 2.50 - 2.90 | Average value: 2.67 Grade Count:6 |
| Dielectric Strength | 19.3 - 22.4 kV/mm | 490 - 570 kV/in | Average value: 21.1 kV/mm Grade Count:10 |
| Dissipation Factor | 0.00100 | 0.00100 | Average value: 0.00100 Grade Count:6 |
| Arc Resistance | 80.0 - 132 sec | 80.0 - 132 sec | Average value: 118 sec Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.8 - 68.4 μm/m-°C | 21.0 - 38.0 μin/in-°F | Average value: 55.0 μm/m-°C Grade Count:13 |
| Thermal Conductivity | 0.159 - 0.187 W/m-K | 1.10 - 1.30 BTU-in/hr-ft2-°F | Average value: 0.180 W/m-K Grade Count:4 |
| Melting Point | 136 - 170 °C | 277 - 338 °F | Average value: 160 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 - 205 °C | 149 - 401 °F | Average value: 142 °C Grade Count:81 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 - 190 °C | 115 - 374 °F | Average value: 117 °C Grade Count:92 |
| Vicat Softening Point | 60.0 - 205 °C | 140 - 401 °F | Average value: 134 °C Grade Count:15 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:44 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 752 °C Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 166 - 240 °C | 330 - 464 °F | Average value: 209 °C Grade Count:16 |
| Nozzle Temperature | 210 - 260 °C | 410 - 500 °F | Average value: 218 °C Grade Count:24 |
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | Average value: 216 °C Grade Count:50 |
| Mold Temperature | 20.0 - 80.0 °C | 68.0 - 176 °F | Average value: 45.8 °C Grade Count:66 |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | Average value: 76.2 °C Grade Count:44 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.09 hour Grade Count:41 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.0568 % Grade Count:22 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 57.8 MPa Grade Count:61 |
| Hold Pressure | 2.07 - 80.0 MPa | 300 - 11600 psi | Average value: 9.94 MPa Grade Count:23 |
| Back Pressure | 0.345 - 58.8 MPa | 50.0 - 8530 psi | Average value: 2.39 MPa Grade Count:28 |