- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.149
- 拉伸強度 [MPa]: 15.0
- 斷裂伸長率 [%]: 20.0
- 彎曲強度 [MPa]: 13.0
- 彎曲模量 [MPa]: 1.40
- 硬度: 45.0
- 熱變形溫度 [℃]: 54.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.48 g/cc | 0.0376 - 0.0535 lb/in3 | Average value: 1.13 g/cc Grade Count:125 |
| Filler Content | 20.0 - 35.0 % | 20.0 - 35.0 % | Average value: 29.4 % Grade Count:66 |
| Water Absorption | 0.0100 - 0.0400 % | 0.0100 - 0.0400 % | Average value: 0.0233 % Grade Count:12 |
| Linear Mold Shrinkage | 0.00600 - 0.0212 cm/cm | 0.00600 - 0.0212 in/in | Average value: 0.0112 cm/cm Grade Count:107 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0150 - 0.0160 cm/cm | 0.0150 - 0.0160 in/in | Average value: 0.0157 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.00850 - 0.0211 cm/cm | 0.00850 - 0.0211 in/in | Average value: 0.0149 cm/cm Grade Count:19 |
| Melt Flow | 0.700 - 230 g/10 min | 0.700 - 230 g/10 min | Average value: 13.1 g/10 min Grade Count:110 |
| Ash | 28.0 - 32.0 % | 28.0 - 32.0 % | Average value: 29.9 % Grade Count:13 |
| 28.0 - 28.0 % @Temperature 900 - 900 °C | 28.0 - 28.0 % @Temperature 1650 - 1650 °F | Average value: 28.0 % Grade Count:1 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 49.0 - 100 | 49.0 - 100 | Average value: 64.6 Grade Count:5 |
| Hardness, Rockwell R | 45.0 - 100 | 45.0 - 100 | Average value: 79.2 Grade Count:20 |
| Hardness, Shore D | 64.0 - 82.0 | 64.0 - 82.0 | Average value: 72.1 Grade Count:16 |
| Tensile Strength, Ultimate | 13.0 - 36.0 MPa | 1890 - 5220 psi | Average value: 26.2 MPa Grade Count:93 |
| Tensile Strength, Yield | 15.0 - 38.0 MPa | 2180 - 5510 psi | Average value: 27.1 MPa Grade Count:45 |
| Elongation at Break | 3.00 - 250 % | 3.00 - 250 % | Average value: 21.8 % Grade Count:65 |
| Elongation at Yield | 2.70 - 80.0 % | 2.70 - 80.0 % | Average value: 8.52 % Grade Count:62 |
| Modulus of Elasticity | 1.50 - 3.79 GPa | 218 - 550 ksi | Average value: 2.57 GPa Grade Count:38 |
| Flexural Yield Strength | 20.0 - 88.0 MPa | 2900 - 12800 psi | Average value: 46.6 MPa Grade Count:74 |
| Flexural Modulus | 1.40 - 4.10 GPa | 203 - 595 ksi | Average value: 2.51 GPa Grade Count:122 |
| 2.60 - 3.70 GPa @Temperature -20.0 - -20.0 °C | 377 - 537 ksi @Temperature -4.00 - -4.00 °F | Average value: 3.15 GPa Grade Count:2 | |
| Izod Impact, Notched | 0.149 - 2.40 J/cm | 0.280 - 4.50 ft-lb/in | Average value: 0.534 J/cm Grade Count:66 |
| 0.300 - 1.00 J/cm @Temperature -40.0 - 0.000 °C | 0.562 - 1.87 ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 0.512 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 0.470 - 13.3 J/cm | 0.881 - 25.0 ft-lb/in | Average value: 4.12 J/cm Grade Count:14 |
| Izod Impact, Notched (ISO) | 2.70 - 40.0 kJ/m2 | 1.28 - 19.0 ft-lb/in2 | Average value: 13.1 kJ/m2 Grade Count:5 |
| 2.10 - 2.10 kJ/m2 @Temperature -40.0 - -40.0 °C | 0.999 - 0.999 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 2.10 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 2.50 J/cm2 - NB | 11.9 ft-lb/in2 - NB | Average value: 5.64 J/cm2 Grade Count:31 |
| 0.900 - 999.9 J/cm2 @Temperature -40.0 - -20.0 °C | 4.28 - 4759 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 2.75 J/cm2 Grade Count:25 | |
| Charpy Impact, Notched | 0.200 - 3.50 J/cm2 | 0.952 - 16.7 ft-lb/in2 | Average value: 0.768 J/cm2 Grade Count:55 |
| 0.100 - 0.600 J/cm2 @Temperature -30.0 - -20.0 °C | 0.476 - 2.86 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.297 J/cm2 Grade Count:43 | |
| Gardner Impact | 0.565 - 21.7 J | 0.417 - 16.0 ft-lb | Average value: 4.47 J Grade Count:22 |
| 5.53626 - 5.53626 J @Temperature -30.0 - -30.0 °C | 4.08334 - 4.08334 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 6.89 J Grade Count:1 | |
| 7.23 - 7.23 J @Temperature -23.0 - -23.0 °C | 5.33 - 5.33 ft-lb @Temperature -9.40 - -9.40 °F | Average value: 6.89 J Grade Count:2 | |
| 7.23 - 7.23 J @Thickness 3.18 - 3.18 mm | 5.33 - 5.33 ft-lb @Thickness 0.125 - 0.125 in | Average value: 6.89 J Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:3 |
| Dielectric Strength | 19.7 - 24.0 kV/mm | 500 - 610 kV/in | Average value: 22.6 kV/mm Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 48.6 - 100 μm/m-°C | 27.0 - 55.6 μin/in-°F | Average value: 77.9 μm/m-°C Grade Count:11 |
| Melting Point | 150 - 182 °C | 302 - 360 °F | Average value: 159 °C Grade Count:19 |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.0 - 144 °C | 129 - 291 °F | Average value: 119 °C Grade Count:97 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 137 °C | 122 - 278 °F | Average value: 73.7 °C Grade Count:103 |
| Vicat Softening Point | 52.0 - 192 °C | 126 - 378 °F | Average value: 109 °C Grade Count:66 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:59 |
| Flammability Test | 1.00 - 125 | 1.00 - 125 | Average value: 75.4 Grade Count:5 |
| Oxygen Index | 21.0 % | 21.0 % | Average value: 21.0 % Grade Count:6 |
| Glow Wire Test | 550 - 750 °C | 1020 - 1380 °F | Average value: 729 °C Grade Count:34 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 227 °C | 380 - 440 °F | Average value: 210 °C Grade Count:3 |
| Nozzle Temperature | 200 - 232 °C | 392 - 450 °F | Average value: 220 °C Grade Count:15 |
| Melt Temperature | 170 - 279 °C | 338 - 534 °F | Average value: 222 °C Grade Count:74 |
| Mold Temperature | 15.0 - 80.0 °C | 59.0 - 176 °F | Average value: 50.5 °C Grade Count:75 |
| Drying Temperature | 51.7 - 100 °C | 125 - 212 °F | Average value: 75.5 °C Grade Count:60 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.75 hour Grade Count:57 |
| Moisture Content | 0.0100 - 0.200 % | 0.0100 - 0.200 % | Average value: 0.0669 % Grade Count:18 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 66.8 MPa Grade Count:61 |
| Hold Pressure | 2.07 - 51.7 MPa | 300 - 7500 psi | Average value: 10.8 MPa Grade Count:12 |
| Back Pressure | 0.345 - 2.00 MPa | 50.0 - 290 psi | Average value: 1.21 MPa Grade Count:42 |