- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.95
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 17.0
- 斷裂伸長率 [%]: 21.0
- 彎曲強度 [MPa]: 13.0
- 彎曲模量 [MPa]: 1.10
- 硬度: 51.0
- 熱變形溫度 [℃]: 74.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 1.24 g/cc | 0.0343 - 0.0448 lb/in3 | Average value: 0.985 g/cc Grade Count:15 |
| Filler Content | 12.0 - 40.0 % | 12.0 - 40.0 % | Average value: 17.6 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00800 - 0.0160 cm/cm | 0.00800 - 0.0160 in/in | Average value: 0.0109 cm/cm Grade Count:15 |
| Melt Flow | 3.00 - 20.0 g/10 min | 3.00 - 20.0 g/10 min | Average value: 12.6 g/10 min Grade Count:14 |
| Ash | 10.0 % | 10.0 % | Average value: 10.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 51.0 - 95.0 | 51.0 - 95.0 | Average value: 78.2 Grade Count:10 |
| Hardness, Shore D | 69.0 - 75.0 | 69.0 - 75.0 | Average value: 71.0 Grade Count:3 |
| Tensile Strength, Ultimate | 13.0 - 35.0 MPa | 1890 - 5080 psi | Average value: 24.1 MPa Grade Count:13 |
| Tensile Strength, Yield | 17.0 - 37.0 MPa | 2470 - 5370 psi | Average value: 29.8 MPa Grade Count:12 |
| Elongation at Break | 17.0 - 27.0 % | 17.0 - 27.0 % | Average value: 21.2 % Grade Count:10 |
| Elongation at Yield | 5.00 - 8.00 % | 5.00 - 8.00 % | Average value: 6.20 % Grade Count:10 |
| Modulus of Elasticity | 1.10 - 1.90 GPa | 160 - 276 ksi | Average value: 1.64 GPa Grade Count:9 |
| Flexural Yield Strength | 21.0 - 48.0 MPa | 3050 - 6960 psi | Average value: 36.6 MPa Grade Count:10 |
| Flexural Modulus | 1.10 - 6.40 GPa | 160 - 928 ksi | Average value: 2.06 GPa Grade Count:16 |
| Izod Impact, Notched | 0.320 - 2.99 J/cm | 0.600 - 5.60 ft-lb/in | Average value: 0.819 J/cm Grade Count:16 |
| Gardner Impact | 0.339 - 4.07 J | 0.250 - 3.00 ft-lb | Average value: 2.82 J Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.4 - 124 °C | 166 - 255 °F | Average value: 102 °C Grade Count:16 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 - 65.6 °C | 120 - 150 °F | Average value: 58.3 °C Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | Average value: 216 °C Grade Count:3 |
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | Average value: 213 °C Grade Count:3 |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | Average value: 37.8 °C Grade Count:3 |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | Average value: 73.9 °C Grade Count:3 |
| Dry Time | 1.00 - 2.00 hour | 1.00 - 2.00 hour | Average value: 1.50 hour Grade Count:3 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:3 |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | Average value: 6.55 MPa Grade Count:3 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:3 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:3 |