- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 0.22
- 缺口沖擊強度: 2.24
- 拉伸強度 [MPa]: 48.3
- 斷裂伸長率 [%]: 62.1
- 彎曲強度 [MPa]: 41.4
- 彎曲模量 [MPa]: 1.93
- 硬度: 46.0
- 熱變形溫度 [℃]: 102.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.29 g/cc | 0.0405 - 0.0466 lb/in3 | Average value: 1.19 g/cc Grade Count:26 |
| Water Absorption | 0.220 - 0.260 % | 0.220 - 0.260 % | Average value: 0.251 % Grade Count:12 |
| Linear Mold Shrinkage | 0.00300 - 0.00900 cm/cm | 0.00300 - 0.00900 in/in | Average value: 0.00624 cm/cm Grade Count:25 |
| Melt Flow | 1.90 - 7.90 g/10 min | 1.90 - 7.90 g/10 min | Average value: 3.85 g/10 min Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44.0 - 55.0 | 44.0 - 55.0 | Average value: 48.5 Grade Count:6 |
| Hardness, Rockwell R | 46.0 | 46.0 | Average value: 46.0 Grade Count:3 |
| Tensile Strength, Ultimate | 41.4 - 61.0 MPa | 6000 - 8850 psi | Average value: 49.7 MPa Grade Count:22 |
| Tensile Strength, Yield | 48.3 - 62.7 MPa | 7010 - 9090 psi | Average value: 55.7 MPa Grade Count:4 |
| Elongation at Break | 10.0 - 88.0 % | 10.0 - 88.0 % | Average value: 26.7 % Grade Count:25 |
| Elongation at Yield | 3.70 - 4.70 % | 3.70 - 4.70 % | Average value: 4.23 % Grade Count:6 |
| Modulus of Elasticity | 1.72 - 2.60 GPa | 250 - 377 ksi | Average value: 2.18 GPa Grade Count:25 |
| Flexural Yield Strength | 62.1 - 91.7 MPa | 9000 - 13300 psi | Average value: 78.0 MPa Grade Count:26 |
| Flexural Modulus | 1.93 - 2.41 GPa | 280 - 350 ksi | Average value: 2.18 GPa Grade Count:25 |
| Izod Impact, Notched | 2.24 - 16.0 J/cm | 4.20 - 30.0 ft-lb/in | Average value: 9.69 J/cm Grade Count:26 |
| 2.1356 - 9.12969 J/cm @Temperature 0.000 - 0.000 °C | 4.0009 - 17.1037 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 5.63 J/cm Grade Count:2 | |
| 2.1356 - 9.12969 J/cm @Diameter 6.35 - 6.35 mm | 4.0009 - 17.1037 ft-lb/in @Diameter 0.250 - 0.250 in | Average value: 5.63 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 20.3 - 5340 J/cm | 38.0 - 10000 ft-lb/in | Average value: 21.0 J/cm Grade Count:16 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 9.90e+10 ohm-cm | 1.00e+8 - 9.90e+10 ohm-cm | Average value: 2.02e+10 ohm-cm Grade Count:6 |
| Surface Resistance | 1.00e+9 - 9.90e+11 ohm | 1.00e+9 - 9.90e+11 ohm | Average value: 1.64e+11 ohm Grade Count:6 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:6 |
| Dielectric Constant | 2.72 | 2.72 | Average value: 2.72 Grade Count:3 |
| Dissipation Factor | 0.00900 | 0.00900 | Average value: 0.00900 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 93.6 μm/m-°C | 52.0 μin/in-°F | Average value: 93.6 μm/m-°C Grade Count:6 |
| 93.6 - 93.6 μm/m-°C @Temperature 0.000 - 100 °C | 52.0 - 52.0 μin/in-°F @Temperature 32.0 - 212 °F | Average value: 93.6 μm/m-°C Grade Count:3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 - 123 °C | 215 - 253 °F | Average value: 114 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 - 123 °C | 180 - 253 °F | Average value: 99.7 °C Grade Count:19 |
| Vicat Softening Point | 119 - 152 °C | 246 - 306 °F | Average value: 136 °C Grade Count:6 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:20 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 0.000 % | 0.000 % | Average value: 0.000 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 249 °C | 380 - 480 °F | Average value: 222 °C Grade Count:9 |
| Melt Temperature | 199 - 266 °C | 390 - 510 °F | Average value: 244 °C Grade Count:14 |
| Mold Temperature | 32.2 - 98.9 °C | 90.0 - 210 °F | Average value: 55.4 °C Grade Count:23 |
| Drying Temperature | 82.2 °C | 180 °F | Average value: 82.2 °C Grade Count:13 |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | Average value: 4.27 hour Grade Count:13 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:10 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:10 |
| Injection Pressure | 33.1 - 103 MPa | 4800 - 15000 psi | Average value: 71.2 MPa Grade Count:20 |