- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 28.0
- 斷裂伸長率 [%]: 41.2
- 彎曲強度 [MPa]: 32.0
- 彎曲模量 [MPa]: 1.36
- 硬度: 61.0
- 熱變形溫度 [℃]: 78.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.19 g/cc | 0.0376 - 0.0430 lb/in3 | Average value: 1.15 g/cc Grade Count:125 |
| Volatiles | 1.00 % | 1.00 % | Average value: 1.00 % Grade Count:6 |
| Water Absorption | 0.100 - 2.00 % | 0.100 - 2.00 % | Average value: 0.366 % Grade Count:61 |
| Moisture Absorption at Equilibrium | 0.300 - 0.400 % | 0.300 - 0.400 % | Average value: 0.360 % Grade Count:7 |
| Water Absorption at Saturation | 0.300 % | 0.300 % | Average value: 0.300 % Grade Count:6 |
| Particle Mesh Size | 30.0 Mesh | 30.0 Mesh | Average value: 30.0 Mesh Grade Count:6 |
| Viscosity | 975000 - 975000 cP @Temperature 240 - 240 °C | 975000 - 975000 cP @Temperature 464 - 464 °F | Average value: 975000 cP Grade Count:1 |
| 975000 - 975000 cP @Shear Rate 100 - 100 1/s | 975000 - 975000 cP @Shear Rate 100 - 100 1/s | Average value: 975000 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00200 - 0.00800 cm/cm | 0.00200 - 0.00800 in/in | Average value: 0.00504 cm/cm Grade Count:104 |
| Melt Flow | 0.700 - 16.0 g/10 min | 0.700 - 16.0 g/10 min | Average value: 4.18 g/10 min Grade Count:124 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 20.0 - 95.0 | 20.0 - 95.0 | Average value: 56.4 Grade Count:57 |
| Hardness, Rockwell R | 61.0 - 117 | 61.0 - 117 | Average value: 78.6 Grade Count:8 |
| Tensile Strength, Ultimate | 32.0 - 82.0 MPa | 4640 - 11900 psi | Average value: 50.0 MPa Grade Count:107 |
| 45.6 - 47.8 MPa @Temperature 18.0 - 18.0 °C | 6610 - 6930 psi @Temperature 64.4 - 64.4 °F | Average value: 46.5 MPa Grade Count:6 | |
| 45.6 - 47.8 MPa @Time 86400 - 86400 sec | 6610 - 6930 psi @Time 24.0 - 24.0 hour | Average value: 46.5 MPa Grade Count:6 | |
| Tensile Strength, Yield | 28.0 - 60.0 MPa | 4060 - 8700 psi | Average value: 42.2 MPa Grade Count:17 |
| Elongation at Break | 1.90 - 90.0 % | 1.90 - 90.0 % | Average value: 30.0 % Grade Count:118 |
| Elongation at Yield | 1.90 - 40.0 % | 1.90 - 40.0 % | Average value: 5.76 % Grade Count:38 |
| Modulus of Elasticity | 1.38 - 3.52 GPa | 200 - 510 ksi | Average value: 2.13 GPa Grade Count:92 |
| Flexural Yield Strength | 41.2 - 105 MPa | 5970 - 15200 psi | Average value: 70.0 MPa Grade Count:110 |
| Flexural Modulus | 1.36 - 3.38 GPa | 198 - 490 ksi | Average value: 2.11 GPa Grade Count:71 |
| Izod Impact, Notched | 0.200 - 2.45 J/cm | 0.375 - 4.59 ft-lb/in | Average value: 0.585 J/cm Grade Count:94 |
| 0.240255 - 0.37373 J/cm @Temperature 0.000 - 0.000 °C | 0.450096 - 0.70015 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.330 J/cm Grade Count:6 | |
| 0.260 - 0.590 J/cm @Temperature 0.000 - 0.000 °C | 0.487 - 1.11 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.330 J/cm Grade Count:2 | |
| 0.260 - 0.590 J/cm @Thickness 6.35 - 6.35 mm | 0.487 - 1.11 ft-lb/in @Thickness 0.250 - 0.250 in | Average value: 0.330 J/cm Grade Count:2 | |
| 0.210 - 0.64068 J/cm @Diameter 6.35 - 6.35 mm | 0.393 - 1.2003 ft-lb/in @Diameter 0.250 - 0.250 in | Average value: 0.330 J/cm Grade Count:10 | |
| 0.210 - 0.64068 J/cm @Temperature 0.000 - 0.000 °C | 0.393 - 1.2003 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.330 J/cm Grade Count:10 | |
| Izod Impact, Unnotched | 1.60 J/cm - NB | 3.00 ft-lb/in - NB | Average value: 3.92 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 2.10 - 8.00 kJ/m2 | 0.999 - 3.81 ft-lb/in2 | Average value: 4.43 kJ/m2 Grade Count:19 |
| Izod Impact, Unnotched (ISO) | 1.50 - 41.7 kJ/m2 | 0.714 - 19.8 ft-lb/in2 | Average value: 21.8 kJ/m2 Grade Count:9 |
| 14.6 - 29.0 kJ/m2 @Temperature 0.000 - 0.000 °C | 6.95 - 13.8 ft-lb/in2 @Temperature 32.0 - 32.0 °F | Average value: 24.1 kJ/m2 Grade Count:4 | |
| 27.6 - 28.3 kJ/m2 @Temperature 0.000 - 0.000 °C | 13.1 - 13.5 ft-lb/in2 @Temperature 32.0 - 32.0 °F | Average value: 24.1 kJ/m2 Grade Count:6 | |
| 27.6 - 28.3 kJ/m2 @Time 86400 - 86400 sec | 13.1 - 13.5 ft-lb/in2 @Time 24.0 - 24.0 hour | Average value: 24.1 kJ/m2 Grade Count:6 | |
| Charpy Impact Unnotched | 2.10 - 8.00 J/cm2 | 9.99 - 38.1 ft-lb/in2 | Average value: 5.82 J/cm2 Grade Count:18 |
| Charpy Impact, Notched | 0.210 - 5.40 J/cm2 | 0.999 - 25.7 ft-lb/in2 | Average value: 1.36 J/cm2 Grade Count:26 |
| Gardner Impact | 1.58 - 11.0 J | 1.17 - 8.11 ft-lb | Average value: 4.61 J Grade Count:47 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+15 ohm-cm | 1.00e+14 - 1.00e+15 ohm-cm | Average value: 7.00e+14 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | Average value: 1.00e+14 ohm Grade Count:7 |
| Dielectric Constant | 2.90 - 3.90 | 2.90 - 3.90 | Average value: 3.30 Grade Count:15 |
| Dielectric Strength | 15.0 - 60.0 kV/mm | 381 - 1520 kV/in | Average value: 30.0 kV/mm Grade Count:15 |
| Dissipation Factor | 0.0300 - 0.0500 | 0.0300 - 0.0500 | Average value: 0.0386 Grade Count:15 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 - 123 μm/m-°C | 33.3 - 68.3 μin/in-°F | Average value: 90.1 μm/m-°C Grade Count:88 |
| 72.0 - 93.6 μm/m-°C @Temperature 0.000 - 156 °C | 40.0 - 52.0 μin/in-°F @Temperature 32.0 - 312 °F | Average value: 78.6 μm/m-°C Grade Count:6 | |
| Specific Heat Capacity | 1.90 - 2.30 J/g-°C @Temperature 100 - 175 °C | 0.454 - 0.550 BTU/lb-°F @Temperature 212 - 347 °F | Average value: 2.10 J/g-°C Grade Count:1 |
| Thermal Conductivity | 0.202 - 0.220 W/m-K | 1.40 - 1.53 BTU-in/hr-ft2-°F | Average value: 0.210 W/m-K Grade Count:5 |
| Maximum Service Temperature, Air | 50.0 - 90.0 °C | 122 - 194 °F | Average value: 72.9 °C Grade Count:14 |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 - 98.0 °C | 172 - 208 °F | Average value: 87.8 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 - 111 °C | 163 - 232 °F | Average value: 84.4 °C Grade Count:114 |
| Vicat Softening Point | 82.0 - 115 °C | 180 - 239 °F | Average value: 100 °C Grade Count:132 |
| Annealing Point | 60.0 - 70.0 °C | 140 - 158 °F | Average value: 65.0 °C Grade Count:8 |
| Heat Distortion Temperature | 80.0 - 97.0 °C | 176 - 207 °F | Average value: 90.3 °C Grade Count:8 |
| Flammability, UL94 | HB | HB | Grade Count:61 |
| Oxygen Index | 18.0 - 19.0 % | 18.0 - 19.0 % | Average value: 18.2 % Grade Count:6 |
| Glow Wire Test | 650 °C | 1200 °F | Average value: 650 °C Grade Count:19 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 - 1.57 | 1.49 - 1.57 | Average value: 1.50 Grade Count:51 |
| Haze | 0.500 - 98.0 % | 0.500 - 98.0 % | Average value: 5.06 % Grade Count:93 |
| Yellow Index | -1.50 - 5.50 % | -1.50 - 5.50 % | Average value: 0.879 % Grade Count:19 |
| Transmission, Visible | 0.000 - 92.0 % | 0.000 - 92.0 % | Average value: 86.3 % Grade Count:116 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 250 °C | 410 - 482 °F | Average value: 230 °C Grade Count:8 |
| Melt Temperature | 179 - 260 °C | 354 - 500 °F | Average value: 229 °C Grade Count:41 |
| Mold Temperature | 27.0 - 107 °C | 80.6 - 225 °F | Average value: 61.1 °C Grade Count:39 |
| Drying Temperature | 60.0 - 105 °C | 140 - 221 °F | Average value: 80.0 °C Grade Count:33 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.75 hour Grade Count:32 |
| Injection Pressure | 49.0 - 108 MPa | 7110 - 15700 psi | Average value: 79.4 MPa Grade Count:9 |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | Average value: 0.739 MPa Grade Count:7 |