- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.147
- 拉伸強度 [MPa]: 45.0
- 斷裂伸長率 [%]: 38.0
- 彎曲強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 1.20
- 熱變形溫度 [℃]: 81.0
- 透光率 [%]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.19 g/cc | 0.0408 - 0.0430 lb/in3 | Average value: 1.18 g/cc Grade Count:37 |
| Water Absorption | 0.200 - 2.00 % | 0.200 - 2.00 % | Average value: 0.663 % Grade Count:23 |
| Moisture Absorption at Equilibrium | 0.300 - 0.360 % | 0.300 - 0.360 % | Average value: 0.312 % Grade Count:5 |
| Water Absorption at Saturation | 0.300 - 2.10 % | 0.300 - 2.10 % | Average value: 1.70 % Grade Count:9 |
| Moisture Expansion | 0.500 - 0.800 % | 0.500 - 0.800 % | Average value: 0.583 % Grade Count:6 |
| Moisture Vapor Transmission | 55.0 - 56.0 cc-mm/m2-24hr-atm | 140 - 142 cc-mil/100 in2-24hr-atm | Average value: 55.3 cc-mm/m2-24hr-atm Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.00800 cm/cm | 0.00200 - 0.00800 in/in | Average value: 0.00468 cm/cm Grade Count:11 |
| Melt Flow | 0.500 - 7.00 g/10 min | 0.500 - 7.00 g/10 min | Average value: 2.16 g/10 min Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45.0 - 101 | 45.0 - 101 | Average value: 79.9 Grade Count:18 |
| Ball Indentation Hardness | 100 - 175 MPa | 14500 - 25400 psi | Average value: 149 MPa Grade Count:8 |
| Tensile Strength, Ultimate | 29.0 - 75.0 MPa | 4210 - 10900 psi | Average value: 58.4 MPa Grade Count:31 |
| 35.0 - 100 MPa @Temperature -40.0 - 70.0 °C | 5080 - 14500 psi @Temperature -40.0 - 158 °F | Average value: 67.5 MPa Grade Count:4 | |
| Tensile Strength, Yield | 45.0 - 86.0 MPa | 6530 - 12500 psi | Average value: 73.7 MPa Grade Count:5 |
| Elongation at Break | 3.50 - 59.0 % | 3.50 - 59.0 % | Average value: 16.1 % Grade Count:29 |
| Elongation at Yield | 4.00 - 6.00 % | 4.00 - 6.00 % | Average value: 5.25 % Grade Count:4 |
| Modulus of Elasticity | 1.80 - 3.30 GPa | 261 - 479 ksi | Average value: 2.96 GPa Grade Count:19 |
| Flexural Yield Strength | 38.0 - 142 MPa | 5510 - 20600 psi | Average value: 92.7 MPa Grade Count:29 |
| Flexural Modulus | 1.20 - 3.38 GPa | 174 - 490 ksi | Average value: 2.60 GPa Grade Count:18 |
| Compressive Yield Strength | 103 MPa | 14900 psi | Average value: 103 MPa Grade Count:4 |
| Poissons Ratio | 0.370 - 0.430 | 0.370 - 0.430 | Average value: 0.402 Grade Count:6 |
| Fatigue Strength | 38.0 MPa | 5510 psi | Average value: 38.0 MPa Grade Count:3 |
| Shear Modulus | 0.629 - 1.70 GPa | 91.2 - 247 ksi | Average value: 1.08 GPa Grade Count:6 |
| Izod Impact, Notched | 0.147 - 0.588 J/cm | 0.275 - 1.10 ft-lb/in | Average value: 0.309 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 1.60 - 8.10 kJ/m2 | 0.761 - 3.85 ft-lb/in2 | Average value: 4.20 kJ/m2 Grade Count:15 |
| Charpy Impact Unnotched | 1.00 J/cm2 - NB | 4.76 ft-lb/in2 - NB | Average value: 3.90 J/cm2 Grade Count:21 |
| Charpy Impact, Notched | 0.200 - 6.40 J/cm2 | 0.952 - 30.5 ft-lb/in2 | Average value: 0.846 J/cm2 Grade Count:16 |
| Falling Dart Impact | 10.8 - 20.6 J | 8.00 - 15.2 ft-lb | Average value: 14.9 J Grade Count:3 |
| Coefficient of Friction | 0.450 - 0.800 | 0.450 - 0.800 | Average value: 0.583 Grade Count:3 |
| Tensile Creep Modulus, 1 hour | 1400 - 2700 MPa | 203000 - 392000 psi | Average value: 2350 MPa Grade Count:4 |
| Tensile Creep Modulus, 1000 hours | 1000 - 1800 MPa | 145000 - 261000 psi | Average value: 1580 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+15 ohm-cm | 1.00e+14 - 1.00e+15 ohm-cm | Average value: 7.60e+14 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+12 - 1.00e+14 ohm | 1.00e+12 - 1.00e+14 ohm | Average value: 8.08e+13 ohm Grade Count:13 |
| Shielding Effectiveness | 26.0 - 33.0 dB | 26.0 - 33.0 dB | Average value: 30.7 dB Grade Count:5 |
| Dielectric Constant | 2.80 - 4.00 | 2.80 - 4.00 | Average value: 3.39 Grade Count:11 |
| Dielectric Strength | 15.0 - 60.0 kV/mm | 381 - 1520 kV/in | Average value: 25.7 kV/mm Grade Count:13 |
| Dissipation Factor | 0.0300 - 0.0600 | 0.0300 - 0.0600 | Average value: 0.0445 Grade Count:11 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 - 110 μm/m-°C | 33.3 - 61.1 μin/in-°F | Average value: 73.5 μm/m-°C Grade Count:20 |
| 72.0 - 72.0 μm/m-°C @Temperature 0.000 - 156 °C | 40.0 - 40.0 μin/in-°F @Temperature 32.0 - 312 °F | Average value: 72.0 μm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | Average value: 1.47 J/g-°C Grade Count:8 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft2-°F | Average value: 0.190 W/m-K Grade Count:4 |
| Maximum Service Temperature, Air | 65.0 - 180 °C | 149 - 356 °F | Average value: 98.9 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 - 101 °C | 178 - 214 °F | Average value: 94.2 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 103 °C | 140 - 217 °F | Average value: 88.3 °C Grade Count:24 |
| Vicat Softening Point | 66.0 - 113 °C | 151 - 235 °F | Average value: 97.4 °C Grade Count:34 |
| Glass Transition Temp, Tg | 105 - 110 °C | 221 - 230 °F | Average value: 107 °C Grade Count:3 |
| Flammability, UL94 | HB | HB | Grade Count:11 |
| Flash Point | 430 °C | 806 °F | Average value: 430 °C Grade Count:4 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 - 1.49 | 1.49 - 1.49 | Average value: 1.49 Grade Count:20 |
| Haze | 0.200 - 3.00 % | 0.200 - 3.00 % | Average value: 1.10 % Grade Count:10 |
| Transmission, Visible | 50.0 - 93.0 % | 50.0 - 93.0 % | Average value: 77.9 % Grade Count:31 |
| UV Transmittance | 0.000 - 80.0 % | 0.000 - 80.0 % | Average value: 10.3 % Grade Count:8 |
| Reflection Coefficient, Visible (0-1) | 0.0330 - 0.0400 | 0.0330 - 0.0400 | Average value: 0.0391 Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 270 °C | 158 - 518 °F | Average value: 135 °C Grade Count:9 |
| Nozzle Temperature | 220 - 245 °C | 428 - 473 °F | Average value: 233 °C Grade Count:3 |
| Adapter Temperature | 230 - 240 °C | 446 - 464 °F | Average value: 235 °C Grade Count:3 |
| Die Temperature | 220 - 240 °C | 428 - 464 °F | Average value: 230 °C Grade Count:3 |
| Melt Temperature | 150 - 249 °C | 302 - 480 °F | Average value: 218 °C Grade Count:5 |
| Mold Temperature | 32.2 - 90.0 °C | 90.0 - 194 °F | Average value: 64.5 °C Grade Count:7 |
| Roll Temperature | 80.0 - 100 °C | 176 - 212 °F | Average value: 90.0 °C Grade Count:3 |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Average value: 77.3 °C Grade Count:7 |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | Average value: 4.14 hour Grade Count:7 |
| Injection Pressure | 78.4 - 147 MPa | 11400 - 21300 psi | Average value: 110 MPa Grade Count:5 |
| Screw Speed | 40.0 - 80.0 rpm | 40.0 - 80.0 rpm | Average value: 60.0 rpm Grade Count:3 |