- 熔體流動(dòng)速率 [g/10min]: 0.55
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Vinyl Acetate Content | 6.5 % | 6.5 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.55 g/10 min | 0.55 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Dart Drop | 18.9 g/micron | 480 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 25.5 MPa | 3700 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 103 MPa | 15000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 110 MPa | 16000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.8 % | 4.8 % | ASTM D1003 | ||
| Gloss | 74 % | 74 % | at 45o; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||