- 熔體流動速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.934
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ASTM-D1505 | ||
| Melt Flow | 0.55 g/10 min | 0.55 g/10 min | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 450 % | 450 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 950 % | 950 % | ASTM-D882 | ||
| Dart Drop | 11.4 g/micron | 290 g/mil | ASTM-D1709 | ||
| Dart drop Test | 580 g | 1.28 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 29.6 MPa | 4290 psi | ASTM-D882 | ||
| 1% Secant Modulus, MD | 75.8 MPa | 11000 psi | ASTM-D882 | ||
| 1% Secant Modulus, TD | 89.6 MPa | 13000 psi | ASTM-D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 94.0 °C | 201 °F | Peak DSC; ASTM D-3418 | ||
| Vicat Softening Point | 76.0 °C | 169 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM-D1003 | ||
| Gloss | 70 % | 70 % | Specular; Angle 45°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | BUR > 1.5:1 | ||
| Descriptive Properties | |||||
| Process | Film | ||||
| Region | US & Canada | ||||