- 熔體流動速率 [g/10min]: 2.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Vinyl Acetate Content | 6.0 % | 6.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 | ||
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 | ||
| Dart Drop | 7.48 g/micron | 190 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 27.6 MPa | 4000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 131 MPa | 19000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 110 MPa | 16000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.0 % | 5.0 % | ASTM D1003 | ||
| Gloss | 65 % | 65 % | at 45o; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||