- 熔體流動(dòng)速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.94
- 彎曲模量 [MPa]: 48.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 | ||
| Vinyl Acetate Content | 18.5 % | 18.5 % | |||
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 32 | 32 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 | ||
| Elongation at Break | 645 % | 645 % | ASTM D638 | ||
| Flexural Modulus, 1% Secant | 48.3 MPa | 7000 psi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 86.0 °C | 187 °F | Peak; Westlake Method | ||
| Vicat Softening Point | 68.0 °C | 154 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Process | Injection Molding | ||||
| Region | US & Canada | ||||