- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in3 | ASTM D1505 | ||
| Vinyl Acetate Content | 2.5 % | 2.5 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 | ||
| Dart drop Test | 150 g | 0.331 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 152 MPa | 22000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.7 % | 3.7 % | ASTM D1003 | ||
| Gloss | 79 % | 79 % | at 45o; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||