- 熔體流動速率 [g/10min]: 0.5
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.925 g/cc | 0.925 g/cc | ISO 1183 |
| Vinyl Acetate Content | 5.5 % | 5.5 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 45.0 - 300 microns | 1.77 - 11.8 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.50 MPa | 1380 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 8.50 MPa | 1230 psi | ISO 527-3 |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 570 % | 570 % | ISO 527-3 |
| Modulus of Elasticity | 0.160 GPa | 23.2 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.40 g/micron | 86.4 g/mil | ISO 6383-2 |
| Dart drop Test | 340 g | 0.750 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | ISO 11357 |
| Vicat Softening Point | 90.0 °C | 194 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.8 % | 8.8 % | ISO 14782 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 190 °C | 320 - 374 °F | |