- 熔體流動速率 [g/10min]: 3.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.929 g/cc | 0.929 g/cc | ISO 1183 |
| Vinyl Acetate Content | 9.0 % | 9.0 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 20.0 - 100 microns | 0.787 - 3.94 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.80 MPa | 1130 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 6.50 MPa | 943 psi | ISO 527-3 |
| Film Elongation at Break, MD | 380 % | 380 % | ISO 527-3 |
| Film Elongation at Break, TD | 570 % | 570 % | ISO 527-3 |
| Modulus of Elasticity | 0.100 GPa | 14.5 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 3.10 g/micron | 78.7 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.60 g/micron | 91.4 g/mil | ISO 6383-2 |
| Dart drop Test | 400 g | 0.882 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 97.0 °C | 207 °F | ISO 11357 |
| Vicat Softening Point | 79.0 °C | 174 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.5 % | 3.5 % | ISO 14782 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | |