- 熔體流動速率 [g/10min]: 0.55
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Vinyl Acetate Content | 4.0 % | 4.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.55 g/10 min | 0.55 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 225 % | 225 % | ASTM D882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 | ||
| Dart drop Test | 160 g | 0.353 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.8 MPa | 3300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 172 MPa | 25000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 207 MPa | 30000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 13 % | 13 % | ASTM D1003 | ||
| Gloss | 50 % | 50 % | at 45o; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | with BUR of 1.5:1 or higher | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||