- 熔體流動速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ASTM D1505 | ||
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 | ||
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 | ||
| Secant Modulus, MD | 0.159 GPa | 23.1 ksi | ASTM D882 | ||
| Secant Modulus, TD | 0.198 GPa | 28.7 ksi | ASTM D882 | ||
| Film Tensile Strength at Break, MD | 22.8 MPa | 3300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.2 MPa | 2500 psi | ASTM D882 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.