- 熔體流動速率 [g/10min]: 0.7
- 彎曲強度 [MPa]: 17.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.926 - 0.931 g/cc | 0.926 - 0.931 g/cc | ASTM D1505 |
| Melt Flow | 0.70 - 0.90 g/10 min @Load 2.61 kg, Temperature 190 °C | 0.70 - 0.90 g/10 min @Load 5.75 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.7 MPa | 2560 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 400 % | 400 % | 500mm/min, Ultimate; ASTM D638 |
| Film Elongation at Break, TD | 650 % | 650 % | 500mm/min, Ultimate; ASTM D638 |
| Elongation at Break | 650 % | 650 % | 500 mm/min, Ultimate; ASTM D638 |
| 2% Secant Modulus | 0.850 GPa | 123 ksi | 500mm/min; ASTM D638 |
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 280 g | 280 g | ASTM D1922 |
| Dart drop Test | 300 g | 0.662 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.4 MPa | 4410 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 30.4 MPa | 4410 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.5 % | 4.5 % | ASTM D1003 |
| Gloss | 100 % | 100 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 101 °C | 214 °F | 10°C/min; ASTM D3418 |