- 熔體流動速率 [g/10min]: 17.0
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | ISO 62:2008 | ||
| Melt Flow | 17 - 27 g/10 min | 17 - 27 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-3 | ||
| Elongation at Break | >= 400 % | >= 400 % | |||
| Tensile Modulus | 0.00800 GPa | 1.16 ksi | Young's; ISO 527-3 | ||
| Peel Strength | 0.00120 kN/m @Time 0.000 sec | 0.00685 pli @Time 0.000 hour | 180° peel, peel speed is 100 mm/min | ||
| 0.00125 kN/m @Time 1.44e+6 sec | 0.00713 pli @Time 400 hour | 180° peel, peel speed is 100 mm/min | |||
| 0.00132 kN/m @Time 2.88e+6 sec | 0.00753 pli @Time 800 hour | 180° peel, peel speed is 100 mm/min | |||
| 0.00150 kN/m @Time 3.24e+6 sec | 0.00856 pli @Time 900 hour | 180° peel, peel speed is 100 mm/min | |||
| 0.00153 kN/m @Time 7.20e+6 sec | 0.00873 pli @Time 2000 hour | 180° peel, peel speed is 100 mm/min | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Shrinkage, MD | 0.00 % @Temperature 120 °C, Time 180 sec | 0.00 % @Temperature 248 °F, Time 0.0500 hour | Q/LSXC | ||
| Shrinkage, TD | 0.00 % @Temperature 120 °C, Time 180 sec | 0.00 % @Temperature 248 °F, Time 0.0500 hour | Q/LSXC | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.49 | 1.49 | ISO 489 | ||
| Yellow Index | 2.9 % @Time 0.000 sec | 2.9 % @Time 0.000 hour | |||
| 3.0 % @Time 0.000 sec | 3.0 % @Time 0.000 hour | after heat and humidity aging (85°c, 85 RH%) | |||
| 3.5 % @Time 3.60e+6 sec | 3.5 % @Time 1000 hour | after heat and humidity aging (85°c, 85 RH%) | |||
| 3.9 % @Time 3.60e+6 sec | 3.9 % @Time 1000 hour | ||||
| 4.0 % @Time 5.40e+6 sec | 4.0 % @Time 1500 hour | ||||
| 4.9 % @Time 7.20e+6 sec | 4.9 % @Time 2000 hour | ||||
| 5.0 % @Time 7.20e+6 sec | 5.0 % @Time 2000 hour | after heat and humidity aging (85°c, 85 RH%) | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 65.0 - 75.0 °C | 149 - 167 °F | ASTM D148 | ||
| Descriptive Properties | |||||
| Surface Uncured | One Side Embossed | ||||
| Thickness Tolerance | ±0.02 | Q/LSXC | |||