- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.935
- 彎曲強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.0830
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 0.40 g/10 min | 0.40 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 84 | 84 | ASTM D2240 |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0830 GPa | 12.0 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 732 kJ/m2 | 348 ft-lb/in2 | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 92.0 °C | 198 °F | Exxon Method |
| Vicat Softening Point | 77.0 °C | 171 °F | 1000g; ASTM D-1525 |