- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.939
- 彎曲強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 0.0540
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 2.1 g/10 min | 2.1 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 84 | 84 | ASTM D2240 |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0540 GPa | 7.83 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 627 kJ/m2 | 298 ft-lb/in2 | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.0 °C | 187 °F | Exxon Method |
| Vicat Softening Point | 66.0 °C | 151 °F | 1000g; ASTM D-1525 |