- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.926
- 拉伸強度 [MPa]: 5.24
- 彎曲強度 [MPa]: 3.03
- 彎曲模量 [MPa]: 0.0125
- 脆化溫度 [℃]: -85.0
- 透光率 [%]: 4.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 - 0.960 g/cc | 0.0335 - 0.0347 lb/in3 | Average value: 0.942 g/cc Grade Count:44 |
| Moisture Vapor Transmission | 1.30 - 1.65 cc-mm/m2-24hr-atm | 3.30 - 4.19 cc-mil/100 in2-24hr-atm | Average value: 1.44 cc-mm/m2-24hr-atm Grade Count:7 |
| Oxygen Transmission | 185 - 264 cc-mm/m2-24hr-atm | 470 - 671 cc-mil/100 in2-24hr-atm | Average value: 215 cc-mm/m2-24hr-atm Grade Count:7 |
| Viscosity | 1.00e+6 - 2.00e+6 cP @Temperature 190 - 190 °C | 1.00e+6 - 2.00e+6 cP @Temperature 374 - 374 °F | Average value: 1.24e+6 cP Grade Count:5 |
| 1.00e+6 - 2.00e+6 cP @Shear Rate 50.0 - 50.0 1/s | 1.00e+6 - 2.00e+6 cP @Shear Rate 50.0 - 50.0 1/s | Average value: 1.24e+6 cP Grade Count:5 | |
| Vinyl Acetate Content | 6.00 - 33.0 % | 6.00 - 33.0 % | Average value: 19.1 % Grade Count:23 |
| Melt Flow | 0.400 - 43.0 g/10 min | 0.400 - 43.0 g/10 min | Average value: 9.98 g/10 min Grade Count:43 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 55.0 - 96.0 | 55.0 - 96.0 | Average value: 78.2 Grade Count:14 |
| Hardness, Shore D | 19.0 - 45.0 | 19.0 - 45.0 | Average value: 31.5 Grade Count:16 |
| Tensile Strength, Ultimate | 3.03 - 17.0 MPa | 440 - 2470 psi | Average value: 10.2 MPa Grade Count:17 |
| Film Tensile Strength at Yield, MD | 4.00 - 9.00 MPa | 580 - 1310 psi | Average value: 6.08 MPa Grade Count:5 |
| Film Tensile Strength at Yield, TD | 3.70 - 10.0 MPa | 537 - 1450 psi | Average value: 6.74 MPa Grade Count:5 |
| Tensile Strength, Yield | 5.24 - 6.31 MPa | 760 - 915 psi | Average value: 5.69 MPa Grade Count:3 |
| Film Elongation at Break, MD | 360 - 600 % | 360 - 600 % | Average value: 505 % Grade Count:12 |
| Film Elongation at Break, TD | 500 - 653 % | 500 - 653 % | Average value: 572 % Grade Count:12 |
| Elongation at Break | 660 - 800 % | 660 - 800 % | Average value: 768 % Grade Count:17 |
| Elongation at Yield | 170 - 260 % | 170 - 260 % | Average value: 203 % Grade Count:3 |
| Flexural Modulus | 0.0125 - 0.101 GPa | 1.82 - 14.6 ksi | Average value: 0.0460 GPa Grade Count:12 |
| Secant Modulus, MD | 0.0380 - 0.120 GPa | 5.51 - 17.4 ksi | Average value: 0.0698 GPa Grade Count:6 |
| Secant Modulus, TD | 0.0430 - 0.125 GPa | 6.24 - 18.1 ksi | Average value: 0.0708 GPa Grade Count:6 |
| Coefficient of Friction | 0.150 - 3.90 | 0.150 - 3.90 | Average value: 0.926 Grade Count:9 |
| Elmendorf Tear Strength, MD | 3.70 - 4.21 g/micron | 94.0 - 107 g/mil | Average value: 3.91 g/micron Grade Count:7 |
| Elmendorf Tear Strength, TD | 3.70 - 5.24 g/micron | 94.0 - 133 g/mil | Average value: 4.36 g/micron Grade Count:4 |
| Dart drop Test | 85.0 - 700 g | 0.187 - 1.54 lb | Average value: 290 g Grade Count:5 |
| Film Tensile Strength at Break, MD | 15.0 - 31.0 MPa | 2180 - 4500 psi | Average value: 24.0 MPa Grade Count:12 |
| Film Tensile Strength at Break, TD | 13.0 - 39.0 MPa | 1890 - 5660 psi | Average value: 23.9 MPa Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 37.0 - 104 °C | 98.6 - 219 °F | Average value: 75.5 °C Grade Count:40 |
| Vicat Softening Point | 40.0 - 81.0 °C | 104 - 178 °F | Average value: 59.3 °C Grade Count:38 |
| Brittleness Temperature | -85.0 - -77.0 °C | -121 - -107 °F | Average value: -82.3 °C Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.00 - 48.0 % | 2.00 - 48.0 % | Average value: 10.9 % Grade Count:14 |
| Gloss | 22.0 - 109 % | 22.0 - 109 % | Average value: 66.6 % Grade Count:14 |
| Transmission, Visible | 4.50 - 75.0 % | 4.50 - 75.0 % | Average value: 36.8 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 125 - 232 °C | 257 - 450 °F | Average value: 193 °C Grade Count:12 |