三星EM-8250G MPPE，20% Glass Filled
類別：聚合物；熱塑性的；聚苯醚/ PPO；Polyphenylene Ether，20% Glass Filled
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 280 °C |
20 g/10 min @Load 22.0 lb, Temperature 536 °F |
ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 137 MPa | 19900 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.49 GPa | 797 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm |
1.84 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 10000 - 1.00e+7 ohm @Temperature 23.0 °C |
10000 - 1.00e+7 ohm @Temperature 73.4 °F |
50% RH; ASTM D250 |
| Static Decay | <= 0.10 sec @Temperature 23.0 °C |
<= 0.10 sec @Temperature 73.4 °F |
50% RH; JIS L1049 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|