| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183-1 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | b.o. ISO 2577 |
| Melt Flow | 25.62 g/10 min @Load 5.00 kg, Temperature 260 °C |
25.62 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Yield Strength | 65.0 MPa @Strain 3.50 % |
9430 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² @Temperature -20.0 °C |
21.4 ft-lb/in² @Temperature -4.00 °F |
ISO 180-A |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 100 V | 100 V | CTI M; Solution B; IEC 60112 |
| 225 V | 225 V | Solution A; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 122 °C @Load 5.10 kg |
252 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Shrinkage | 0.10 - 0.20 % | 0.10 - 0.20 % | post-shrinkage; b.o. ISO 2577 |
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com