| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183-1 |
| Filler Content | 20.0 % | 20.0 % | Method A; b.o. ISO 3451-1 |
| Moisture Absorption at Equilibrium | 0.150 % | 0.150 % | ISO 62 |
| Water Absorption at Saturation | 0.300 % | 0.300 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00200 - 0.00400 cm/cm | 0.00200 - 0.00400 in/in | 150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577 |
| 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | b.o. ISO 2577 | |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.00700 cm/cm | 0.00500 - 0.00700 in/in | 150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577 |
| Melt Flow | 42.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
42.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1,-2 |
| 3.0 % | 3.0 % | Nominal, 5 mm/min; ISO 527-1,-2 | |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1,-2 |
| 3.00 % | 3.00 % | Flexural strain, 2 mm/min; ISO 178 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A | |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180-U |
| 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180-U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 0.150 @Frequency 1.00e+6 Hz |
0.150 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.60 @Frequency 100 Hz |
3.60 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm |
838 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.00130 @Frequency 100 Hz |
0.00130 @Frequency 100 Hz |
IEC 60250 |
| 0.0144 @Frequency 1.00e+6 Hz |
0.0144 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1,-2 |
| Vicat Softening Point | 140 °C @Load 5.10 kg |
284 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Shrinkage | <= 0.10 % | <= 0.10 % | post-shrinkage; b.o. ISO 2577 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | Injection molding; ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營(yíng)銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報(bào)告（如：物性表，MSDS報(bào)告，UL報(bào)告，COA報(bào)告，SGS報(bào)告，F(xiàn)DA等）！
歡迎新老客戶來(lái)電或QQ咨詢：
聯(lián)系人：李生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com