| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Viscosity | 380000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
380000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
melt viscosity; b.o. ISO 11443-A |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0050 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0050 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Melt Flow | 13.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
13.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 3.95 GPa | 573 ksi | 1 mm/min; ISO 527-1,-2 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
26.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
32.8 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1,-2 |
| Vicat Softening Point | 106 °C @Load 5.10 kg |
223 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 108 °C @Load 5.10 kg |
226 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com