| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 |
| 0.60 % @Temperature 100 °C |
0.60 % @Temperature 212 °F |
ISO 62-1 | |
| Viscosity | 450000 cP @Temperature 400 °C |
450000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 395°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 10.5 cm @Thickness 1.00 mm |
4.13 in @Thickness 0.0394 in |
395°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 88 @Temperature 23.0 °C |
88 @Temperature 73.4 °F |
ISO 868 |
| Tensile Strength at Break | 55.0 MPa @Temperature 275 °C |
7980 psi @Temperature 527 °F |
ISO 527 |
| 65.0 MPa @Temperature 225 °C |
9430 psi @Temperature 437 °F |
ISO 527 | |
| 75.0 MPa @Temperature 175 °C |
10900 psi @Temperature 347 °F |
ISO 527 | |
| 125 MPa @Temperature 125 °C |
18100 psi @Temperature 257 °F |
ISO 527 | |
| 200 MPa @Temperature 23.0 °C |
29000 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 2.9 % @Temperature 23.0 °C |
2.9 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 12.0 GPa @Temperature 23.0 °C |
1740 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 85.0 MPa @Temperature 275 °C |
12300 psi @Temperature 527 °F |
ISO 178 |
| 120 MPa @Temperature 175 °C |
17400 psi @Temperature 347 °F |
ISO 178 | |
| 210 MPa @Temperature 123 °C |
30500 psi @Temperature 253 °F |
ISO 178 | |
| 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 11.0 GPa @Temperature 23.0 °C |
1600 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 50.0 MPa @Temperature 250 °C |
7250 psi @Temperature 482 °F |
ISO 604 |
| 75.0 MPa @Temperature 200 °C |
10900 psi @Temperature 392 °F |
ISO 604 | |
| 180 MPa @Temperature 120 °C |
26100 psi @Temperature 248 °F |
ISO 604 | |
| 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
SO 179/1U |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1000 Hz, Temperature 23.0 °C |
3.2 @Frequency 1000 Hz, Temperature 73.4 °F |
IEC 60250 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
IEC 60250 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 45.0 µm/m-°C @Temperature <=152 °C |
25.0 µin/in-°F @Temperature <=306 °F |
Average below Tg; ISO 11359 |
| 110 µm/m-°C @Temperature >=152 °C |
61.1 µin/in-°F @Temperature >=306 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature <=152 °C |
11.1 µin/in-°F @Temperature <=306 °F |
Below Tg; ISO 11359 |
| 25.0 µm/m-°C @Temperature >=152 °C |
13.9 µin/in-°F @Temperature >=306 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.300 W/m-K @Temperature 23.0 °C |
2.08 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 |
| 0.350 W/m-K @Temperature 23.0 °C |
2.43 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Along flow; ISO 22007-4 | |
| Melting Point | 373 °C | 703 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 360 °C | 680 °F | ISO 75-f |
| Glass Transition Temp, Tg | 152 °C | 306 °F | Onset; ISO 11357 |
| 160 °C | 320 °F | Midpoint; ISO 11357 | |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 395 °C | 743 °F | |
| Mold Temperature | 190 - 215 °C | 374 - 419 °F | |
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |
||
.