| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | |||
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
|||
| Linear Mold Shrinkage, Flow | 0.0011 cm/cm | 0.0011 in/in | 410°C nozzle, 220°C mold | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 410°C nozzle, 220°C mold | ||
| Crystallinity | 40 % | 40 % | DSC | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 106 | 106 | ASTM D785 | ||
| Hardness, Shore D | 91 | 91 | |||
| Tensile Strength at Break | 45.0 MPa @Temperature 250 °C |
6530 psi @Temperature 482 °F |
ASTM D638 | ||
| 55.0 MPa @Temperature 200 °C |
7980 psi @Temperature 392 °F |
ASTM D638 | |||
| 80.0 MPa @Temperature 150 °C |
11600 psi @Temperature 302 °F |
ASTM D638 | |||
| 120 MPa @Temperature 100 °C |
17400 psi @Temperature 212 °F |
ASTM D638 | |||
| 130 - 135 MPa @Temperature 23.0 °C |
18900 - 19600 psi @Temperature 73.4 °F |
ASTM D638 | |||
| 145 MPa @Temperature -10.0 °C |
21000 psi @Temperature 14.0 °F |
ASTM D638 | |||
| 160 MPa @Temperature -50.0 °C |
23200 psi @Temperature -58.0 °F |
ASTM D638 | |||
| Elongation at Break | 1.5 - 2.0 % | 1.5 - 2.0 % | ASTM D638 | ||
| Tensile Modulus | 11.5 GPa | 1670 ksi | ASTM D638 | ||
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 | ||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.400 - 0.450 J/cm | 0.749 - 0.843 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 6.10 J/cm | 11.4 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 370 - 372 °C | 698 - 702 °F | DSC | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 368 °C | 694 °F | |||
| Glass Transition Temp, Tg | 152 - 154 °C | 306 - 309 °F | DSC/onset | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 390 - 425 °C | 734 - 797 °F | |||
| Nozzle Temperature | 425 °C | 797 °F | |||
| Mold Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| De |
|||||
| Hopper/ Throat Temperature | 60-80°C | ||||
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com