| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 25 g/10 min | 25 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 6.0 % | 6.0 % | |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 3.60 J/cm² | 17.1 ft-lb/in² | |
| Tensile Impact Strength | 110 kJ/m² | 52.3 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2000 MPa | 290000 psi | |
| Tensile Creep Modulus, 1000 hours | 2000 MPa | 290000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 2.00e+14 ohm | 2.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 2.0 @Frequency 1e+6 Hz |
2.0 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | |
| Dissipation Factor | 0.00080 @Frequency 100 Hz |
0.00080 @Frequency 100 Hz |
|
| 0.0016 @Frequency 1e+6 Hz |
0.0016 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 225 V | 225 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
| Vicat Softening Point | 190 °C | 374 °F | 50°C/hr/50 N |
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報(bào)告（如：物性表，MSDS報(bào)告，UL報(bào)告，COA報(bào)告，SGS報(bào)告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com