LCP 6635 材料說明：澤尼特«6635 35%礦物/玻璃纖維增強液晶聚合物注射成型。它具有優良的熔接強度和優異的流動特性。
LCP 6635 形式：粒子
LCP 6635 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| Melt Density | 1.39 g/cc | 0.0502 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.030 % | 0.030 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Tensile Stress | 9.28 MPa @Strain 0.230 %, Temperature 180 °C |
1350 psi @Strain 0.230 %, Temperature 356 °F |
|
| 10.7 MPa @Strain 0.320 %, Temperature 200 °C |
1550 psi @Strain 0.320 %, Temperature 392 °F |
||
| 138 MPa @Strain 3.85 %, Temperature -20.0 °C |
20000 psi @Strain 3.85 %, Temperature -4.00 °F |
||
| Elongation at Break | 3.2 % | 3.2 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm² @Temperature 30.0 °C |
19.0 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 7500 MPa | 1.09e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 5500 MPa | 798000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | |
| Melting Point | 335 °C | 635 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | ISO 11357-1,-2,-3 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|