LCP 6130 材料說明：澤尼特«6130是注塑成型的30%玻璃纖維增強液晶聚合物。具有良好的耐沖擊性和良好的熱變形溫度。
LCP 6130 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm | 0.0015 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 13.0 GPa | 1890 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Compressive Strength | 113 MPa | 16400 psi | ISO 604 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
IEC 60250 |
| 0.031 @Frequency 1.00e+6 Hz |
0.031 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C | 1.67 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 300 °C | 572 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 268 °C | 514 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 120 °C | 248 °F | ISO 11357-1,-2,-3 |
| Flammability, UL94 | V-0 @Thickness 0.200 mm |
V-0 @Thickness 0.00787 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| Oxygen Index | 41 % | 41 % | ISO 4589 |