LCP V140 材料說明：LCP／PPS共混。保持最具有改進的熔接強度A130的特點。40%玻璃增強。
LCP V140 形式：粒子
LCP V140 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 96 | 96 | ISO 2039-2 |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5mm/min; ISO 527-2/1A |
| Tensile Stress | 20.83 MPa @Strain 0.130 %, Temperature 23.0 °C |
3021 psi @Strain 0.130 %, Temperature 73.4 °F |
|
| 145.38 MPa @Strain 1.38 %, Temperature 23.0 °C |
21086 psi @Strain 1.38 %, Temperature 73.4 °F |
||
| Elongation at Break | 1.0 % | 1.0 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 |
| Compressive Strength | 134 MPa @Strain 1.00 % |
19400 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 16.0 GPa | 2320 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
IEC 60250 | |
| Arc Resistance | 165 sec | 165 sec | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C | 6.11 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 21.0 µm/m-°C | 11.7 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||