LCP C245GP 材料說明：液晶聚合物樹脂：sepaz LCP樹脂具有傳統塑料的一種獨特的結構和性能沒有想到的。在sepaz LCP以優異的綜合性能和成型效率。sepaz LCP具有獨特的屬性，產品變得更薄，更大的機械強度。sepaz LCP連接器發現使用，傳感器和其他電子元件和CD提取部分，在復印機和傳真辦公和視聽設備部件。
LCP C245GP 加工方法：注塑成型
LCP C245GP 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 135.4 MPa | 19630 psi | ASTM D638 |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| Flexural Strength | 191.3 MPa | 27750 psi | ASTM D790 |
| Flexural Modulus | 18.34 GPa | 2661 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 4.3 @Frequency 1.00e+6 Hz |
4.3 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.60 mm |
533 kV/in @Thickness 0.0630 in |
ASTM D149 |
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz |
0.025 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 352 °C | 666 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 295 °C | 563 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |