| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.995 g/cc | 0.0359 lb/in³ | |||
| 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | |||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ISO 294-4 2577 | ||
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 240 °C |
13 g/10 min @Load 4.76 lb, Temperature 464 °F |
cm³/10min; ISO 1133 | ||
| 13 g/10 min @Load 2.16 kg, Temperature 240 °C |
13 g/10 min @Load 4.76 lb, Temperature 464 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 44 | 44 | 15s; ISO 868 | ||
| <= 49 | <= 49 | ISO 868 | |||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527-1/-2 | ||
| Tensile Stress | 7.80 MPa @Strain 5.00 % |
1130 psi @Strain 5.00 % |
ISO 527-1/-2 | ||
| 9.70 MPa @Strain 10.0 % |
1410 psi @Strain 10.0 % |
ISO 527-1/-2 | |||
| 12.5 MPa @Strain 50.0 % |
1810 psi @Strain 50.0 % |
ISO 527-1/-2 | |||
| 14.0 MPa @Strain 100 % |
2030 psi @Strain 100 % |
ISO 527-1/-2 | |||
| 18.0 MPa @Strain 300 % |
2610 psi @Strain 300 % |
ISO 527-1/-2 | |||
| 0.280 MPa @Strain 0.200 %, Temperature 90.0 °C |
40.6 psi @Strain 0.200 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 0.670 MPa @Strain 0.200 %, Temperature 23.0 °C |
97.2 psi @Strain 0.200 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 1.51 MPa @Strain 0.240 %, Temperature -40.0 °C |
219 psi @Strain 0.240 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 3.90 MPa @Strain 5.68 %, Temperature 90.0 °C |
566 psi @Strain 5.68 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 6.93 MPa @Strain 21.48 %, Temperature 90.0 °C |
1010 psi @Strain 21.48 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 7.69 MPa @Strain 39.3 %, Temperature 90.0 °C |
1120 psi @Strain 39.3 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 10.13 MPa @Strain 10.62 %, Temperature 23.0 °C |
1469 psi @Strain 10.62 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 12.31 MPa @Strain 33.7 %, Temperature 23.0 °C |
1785 psi @Strain 33.7 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 23.18 MPa @Strain 7.28 %, Temperature -40.0 °C |
3362 psi @Strain 7.28 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 26.81 MPa @Strain 18.04 %, Temperature -40.0 °C |
3888 psi @Strain 18.04 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 27.29 MPa @Strain 28.8 %, Temperature -40.0 °C |
3958 psi @Strain 28.8 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Elongation at Break | >= 300 % | >= 300 % | ISO 527-1/-2 | ||
| 600 % | 600 % | Nominal; ISO 527-1/-2 | |||
| Tensile Modulus | 0.295 GPa | 42.8 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 0.350 GPa | 50.8 ksi | ISO 178 | ||
| Secant Modulus | 0.0299 GPa @Strain 41.95 %, Temperature 23.0 °C |
4.34 ksi @Strain 41.95 %, Temperature 73.4 °F |
ISO 11403-1 -2 | ||
| 0.076397 GPa @Strain 35.97 %, Temperature -40.0 °C |
11.081 ksi @Strain 35.97 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 0.0954 GPa @Strain 10.62 %, Temperature 23.0 °C |
13.8 ksi @Strain 10.62 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.125 GPa @Strain 21.63 %, Temperature -40.0 °C |
18.1 ksi @Strain 21.63 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 0.318 GPa @Strain 7.28 %, Temperature -40.0 °C |
46.2 ksi @Strain 7.28 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 0.335 GPa @Strain 0.200 %, Temperature 23.0 °C |
48.6 ksi @Strain 0.200 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.629 GPa @Strain 0.240 %, Temperature -40.0 °C |
91.3 ksi @Strain 0.240 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Tear Strength | 90.0 kN/m | 514 pli | normal; ISO 34-1 | ||
| 110 kN/m | 628 pli | parallel; ISO 34-1 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | ISO 75-1/-2 | ||
| Brittleness Temperature | -100 °C | -148 °F | ISO 974 | ||
| Flame Spread | 24 mm/min @Thickness 1.00 mm |
0.94 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Delivery form | Pellets | ||||
| Emission of organic compounds | 9.3 µgC/g | VDA 277 | |||
| Odour | class 4 | VDA 270 | |||
| Part Marking Code | >TPC-ET+PBT< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | TPC-ET+PBT | ISO 1043 | |||
| Special characteristics | Heat stabilised or stable to heat | ||||
| Light stabilised or stable to light | |||||
| U.V. stabilised or stable to weather | |||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
歡迎新老客戶來電或QQ咨詢：
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com